| 是否进口：否 | 产地：美国 | 厂家(产地)：沙伯基础(原GE) |
| 牌号：FR GLX143 | 销售方式：品牌经销 | 类型：标准料 |
| 加工级别：注塑级 | 特性级别：标准级 | 用途级别：汽车部件、 电子电器部件、 运动器材、 家电部件、 电动工具配件 |
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in? | ISO 1183 |
| Water Absorption | 0.35 % | 0.35 % | 23°C/sat; ISO 62 |
| Moisture Absorption | 0.150 % | 0.150 % | 23°C / 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | SABIC method |
| Melt Flow | 12 g/10 min @Load 1.20 kg, Temperature 300 °C | 12 g/10 min @Load 2.65 lb, Temperature 572 °F | cm?/10 min; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 70.0 MPa | 10200 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 65.0 MPa | 9430 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 120 % | 120 % | 50 mm/min; ISO 527 |
| Elongation at Yield | 6.0 % | 6.0 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 2.35 GPa | 341 ksi | 1mm/min; ISO 527 |
| Flexural Yield Strength | 90.0 MPa | 13100 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.30 GPa | 334 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 70.0 kJ/m? | 33.3 ft-lb/in? | 80*10*3; ISO 180/1A |
| 12.0 kJ/m? @Temperature -30.0 °C | 5.71 ft-lb/in? @Temperature -22.0 °F | 80*10*3; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB | NB | 80*10*3; ISO 180/1U |
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | 80*10*3; ISO 180/1U | |
| Charpy Impact Unnotched | NB | NB | Edgew 80*10*3 sp=62mm; ISO 179/1eU |
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | Edgew 80*10*3 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 7.30 J/cm? | 34.7 ft-lb/in? | Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| 1.40 J/cm? @Temperature -30.0 °C | 6.66 ft-lb/in? @Temperature -22.0 °F | Edgew 80*10*3 sp=62mm; ISO 179/1eA | |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 2.7 @Frequency 50.0 - 60.0 Hz | 2.7 @Frequency 50.0 - 60.0 Hz | IEC 60250 |
| 2.7 @Frequency 1.00e+6 Hz | 2.7 @Frequency 1.00e+6 Hz | IEC 60250 | |
| Dielectric Strength | 15.0 kV/mm @Thickness 1.00 mm | 381 kV/in @Thickness 0.0394 in | shorttime; IEC 60243-1 |
| 17.0 kV/mm @Thickness 3.20 mm | 432 kV/in @Thickness 0.126 in | in oil; IEC 60243-1 | |
| Dissipation Factor | 0.0010 @Frequency 50.0 - 60.0 Hz | 0.0010 @Frequency 50.0 - 60.0 Hz | IEC 60250 |
| 0.010 @Frequency 1.00e+6 Hz | 0.010 @Frequency 1.00e+6 Hz | IEC 60250 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 70.0 ?m/m-°C @Temperature 23.0 - 80.0 °C | 38.9 ?in/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 70.0 ?m/m-°C @Temperature 23.0 - 80.0 °C | 38.9 ?in/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 |
| Thermal Conductivity | 0.200 W/m-K | 1.39 BTU-in/hr-ft?-°F | ISO 8302 |
| Hot Ball Pressure Test | 125 °C | 257 °F | IEC 60695-10-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 136 °C | 277 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| Deflection Temperature at 1.8 MPa (264 psi) | 124 °C | 255 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 125 °C | 257 °F | 1.8 MPa Edgew 120*10*4 sp=100mm; ISO 75/Ae | |
| Vicat Softening Point | 142 °C | 288 °F | Rate B/50; ISO 306 |
| 143 °C | 289 °F | Rate B/120; ISO 306 | |
| UL RTI, Electrical | 130 °C | 266 °F | UL 746B |
| UL RTI, Mechanical with Impact | 125 °C | 257 °F | UL 746B |
| UL RTI, Mechanical without Impact | 125 °C | 257 °F | UL 746B |
| Oxygen Index | 25 % | 25 % | ISO 4589 |
| Glow Wire Test | 850 °C @Thickness 1.00 mm | 1560 °F @Thickness 0.0394 in | IEC 60695-2-12 |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.586 | 1.586 | ISO 489 |
| Haze | <= 0.80 % @Thickness 2.54 mm | <= 0.80 % @Thickness 0.100 in | ASTM D1003 |
| Transmission, Visible | 86 % | 86 % | Luminous Transmittance, clear transparant, 6 mm; ASTM D1003 |
| 87 % | 87 % | Luminous Transmittance, clear transparant, 5 mm; ASTM D1003 | |
| 88 % | 88 % | Luminous Transmittance, clear transparant, 4 mm; ASTM D1003 | |
| 89 % | 89 % | Luminous Transmittance, clear transparant, 3 mm; ASTM D1003 | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Hopper Temperature |
| Nozzle Temperature | 270 - 290 °C | 518 - 554 °F | Injection Molding |
| Zone 1 | 260 - 280 °C | 500 - 536 °F | |
| Zone 2 | 270 - 290 °C | 518 - 554 °F | |
| Zone 3 | 280 - 310 °C | 536 - 590 °F | |
| Melt Temperature | 280 - 310 °C | 536 - 590 °F | |
| Mold Temperature | 80.0 - 110 °C | 176 - 230 °F | |
| Drying Temperature | 120 °C | 248 °F | Injection Molding |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | Injection Molding |
| Moisture Content | 0.020 % | 0.020 % |