| 是否进口：否 | 产地：美国 | 厂家(产地)：沙伯基础(原GE) |
| 牌号：PC0700 | 销售方式：品牌经销 | 类型：标准料 |
| 加工级别：注塑级 | 特性级别：标准级 | 用途级别：汽车部件、 电子电器部件、 运动器材、 家电部件、 电动工具配件 |
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Density | 1.20 g/cc | 0.0434 lb/in? | ISO 1183 |
| Water Absorption | 0.35 % | 0.35 % | 23°C/sat; ISO 62 |
| Moisture Absorption at Equilibrium | 0.35 % | 0.35 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | SABIC method |
| 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm | 0.0050 - 0.0070 in/in @Thickness 0.126 in | SABIC method | |
| Melt Flow | 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C | 6.0 g/10 min @Load 2.65 lb, Temperature 572 °F | cm?/10 min; ISO 1133 |
| 7.0 g/10 min @Load 1.20 kg, Temperature 300 °C | 7.0 g/10 min @Load 2.65 lb, Temperature 572 °F | ASTM D1238 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 120 | 120 | ISO 2039-2 |
| 120 | 120 | ASTM D785 | |
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | 50 mm/min; ISO 527 |
| 63.0 MPa | 9140 psi | 50 mm/min; ASTM D638 | |
| Elongation at Break | >= 70 % | >= 70 % | 50mm/min; ASTM D638 |
| >= 70 % | >= 70 % | 50mm/min; ISO 527 | |
| Elongation at Yield | 6.0 % | 6.0 % | 50 mm/min; ASTM D638 |
| 6.0 % | 6.0 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 2.35 GPa | 341 ksi | 50 mm/min; ASTM D638 |
| 2.35 GPa | 341 ksi | 1mm/min; ISO 527 | |
| Flexural Yield Strength | 90.0 MPa | 13100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 90.0 MPa | 13100 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 2.30 GPa | 334 ksi | 2 mm/min; ISO 178 |
| 2.30 GPa | 334 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 9.00 J/cm | 16.9 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D4812 |
| Izod Impact, Notched (ISO) | 70.0 kJ/m? | 33.3 ft-lb/in? | 80*10*3; ISO 180/1A |
| 12.0 kJ/m? @Temperature -30.0 °C | 5.71 ft-lb/in? @Temperature -22.0 °F | 80*10*3; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB | NB | 80*10*3; ISO 180/1U |
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | 80*10*3; ISO 180/1U | |
| Dart Drop, Total Energy | 65.0 J | 47.9 ft-lb | peak; ASTM D3763 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | ASTM D257 |
| >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 | |
| Dielectric Constant | 3.0 @Frequency 60.0 Hz | 3.0 @Frequency 60.0 Hz | IEC 60250 |
| 3.0 @Frequency 1.00e+6 Hz | 3.0 @Frequency 1.00e+6 Hz | ASTM D150 | |
| 3.0 @Frequency 60.0 Hz | 3.0 @Frequency 60.0 Hz | ASTM D150 | |
| 3.0 @Frequency 1.00e+6 Hz | 3.0 @Frequency 1.00e+6 Hz | IEC 60250 | |
| Dielectric Strength | 27.0 kV/mm @Thickness 1.60 mm | 686 kV/in @Thickness 0.0630 in | IEC 60243-1 |
| 27.0 kV/mm @Thickness 1.60 mm | 686 kV/in @Thickness 0.0630 in | ASTM D149 | |
| Dissipation Factor | 0.0010 @Frequency 60.0 Hz | 0.0010 @Frequency 60.0 Hz | IEC 60250 |
| 0.0010 @Frequency 60.0 Hz | 0.0010 @Frequency 60.0 Hz | ASTM D150 | |
| 0.010 @Frequency 1.00e+6 Hz | 0.010 @Frequency 1.00e+6 Hz | ASTM D150 | |
| 0.010 @Frequency 1.00e+6 Hz | 0.010 @Frequency 1.00e+6 Hz | IEC 60250 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 70.0 ?m/m-°C @Temperature -40.0 - 95.0 °C | 38.9 ?in/in-°F @Temperature -40.0 - 203 °F | ASTM E831 |
| 70.0 ?m/m-°C @Temperature 23.0 - 80.0 °C | 38.9 ?in/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 | |
| Thermal Conductivity | 0.200 W/m-K | 1.39 BTU-in/hr-ft?-°F | ASTM C177 |
| 0.200 W/m-K | 1.39 BTU-in/hr-ft?-°F | ISO 8302 | |
| Hot Ball Pressure Test | 125 °C | 257 °F | IEC 60695-10-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 138 °C | 280 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 138 °C @Thickness 3.20 mm | 280 °F @Thickness 0.126 in | ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 261 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 127 °C @Thickness 3.20 mm | 261 °F @Thickness 0.126 in | ASTM D648 | |
| Vicat Softening Point | 144 °C | 291 °F | Rate B/50; ISO 306 |
| 144 °C | 291 °F | Rate B/50; ASTM D1525 | |
| Flammability, UL94 | V-2 @Thickness 1.60 mm | V-2 @Thickness 0.0630 in | UL 94 |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.586 | 1.586 | ASTM D542 |
| 1.586 | 1.586 | ISO 489 | |
| Haze | <= 0.80 % @Thickness 2.54 mm | <= 0.80 % @Thickness 0.100 in | ASTM D1003 |
| Transmission, Visible | 88 - 90 % @Thickness 2.54 mm | 88 - 90 % @Thickness 0.100 in | ASTM D1003 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Hopper Temperature |
| Nozzle Temperature | 280 - 310 °C | 536 - 590 °F | Injection Molding |
| Zone 1 | 270 - 300 °C | 518 - 572 °F | |
| Zone 2 | 280 - 310 °C | 536 - 590 °F | |
| Zone 3 | 290 - 320 °C | 554 - 608 °F | |
| Melt Temperature | 290 - 320 °C | 554 - 608 °F | |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | |
| Drying Temperature | 120 °C | 248 °F | Injection Molding |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | Injection Molding |
| Moisture Content | 0.020 % | 0.020 % |