| 是否进口：否 | 产地：美国 | 厂家(产地)：沙伯基础(原GE) |
| 牌号： FR 505R | 销售方式：品牌经销 | 类型：标准料 |
| 加工级别：注塑级 | 特性级别：标准级 | 用途级别：汽车部件、 电子电器部件、 运动器材、 家电部件、 电动工具配件 |
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.26 g/cc | 1.26 g/cc | ASTM D792 |
| Density | 1.25 g/cc | 0.0452 lb/in? | ISO 1183 |
| Water Absorption | 0.12 % | 0.12 % | 24 hours; ASTM D570 |
| 0.31 % | 0.31 % | 23°C/sat; ISO 62 | |
| Moisture Absorption | 0.130 % | 0.130 % | 23°C / 50% RH; ISO 62 |
| 0.130 % | 0.130 % | 50% RH, 24 hrs; ASTM D570 | |
| Moisture Absorption at Equilibrium | 0.31 % | 0.31 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | SABIC method |
| 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm | 0.0050 - 0.0070 in/in @Thickness 0.126 in | SABIC method | |
| Melt Flow | 7.0 g/10 min @Load 1.20 kg, Temperature 300 °C | 7.0 g/10 min @Load 2.65 lb, Temperature 572 °F | ASTM D1238 |
| 7.0 g/10 min @Load 1.20 kg, Temperature 300 °C | 7.0 g/10 min @Load 2.65 lb, Temperature 572 °F | cm?/10 min; ISO 1133 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 85 | 85 | ASTM D785 |
| Hardness, Rockwell R | 124 | 124 | ASTM D785 |
| Ball Indentation Hardness | 115 MPa | 16700 psi | ISO 2039-1 |
| Tensile Strength at Break | 45.0 MPa | 6530 psi | 5 mm/min; ISO 527 |
| 48.0 MPa | 6960 psi | 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | 5 mm/min; ISO 527 |
| 63.0 MPa | 9140 psi | 5 mm/min; ASTM D638 | |
| Elongation at Break | 7.0 % | 7.0 % | 5 mm/min; ISO 527 |
| 12 % | 12 % | 5 mm/min; ASTM D638 | |
| Elongation at Yield | 3.0 % | 3.0 % | 5 mm/min; ASTM D638 |
| 5.0 % | 5.0 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 3.30 GPa | 479 ksi | 1mm/min; ISO 527 |
| 3.93 GPa | 570 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 108 MPa | 15700 psi | brk, 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Yield Strength | 95.0 MPa | 13800 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 3.40 GPa | 493 ksi | 2 mm/min; ISO 178 |
| 3.53 GPa | 512 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 1.07 J/cm | 2.00 ft-lb/in | ASTM D256 |
| 0.800 J/cm @Temperature -30.0 °C | 1.50 ft-lb/in @Temperature -22.0 °F | ASTM D256 | |
| Izod Impact, Unnotched | 16.02 J/cm | 30.01 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m? | 3.81 ft-lb/in? | 80*10*4; ISO 180/1A |
| 10.0 kJ/m? | 4.76 ft-lb/in? | 80*10*3; ISO 180/1A | |
| 8.00 kJ/m? @Temperature -30.0 °C | 3.81 ft-lb/in? @Temperature -22.0 °F | 80*10*3; ISO 180/1A | |
| 8.00 kJ/m? @Temperature -30.0 °C | 3.81 ft-lb/in? @Temperature -22.0 °F | 80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB | NB | 80*10*4; ISO 180/1U |
| NB | NB | 80*10*3; ISO 180/1U | |
| 130 kJ/m? @Temperature -30.0 °C | 61.9 ft-lb/in? @Temperature -22.0 °F | 80*10*3; ISO 180/1U | |
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | 80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | NB | NB | Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| NB | NB | Edgew 80*10*3 sp=62mm; ISO 179/1eU | |
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | Edgew 80*10*3 sp=62mm; ISO 179/1eU | |
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 0.900 J/cm? | 4.28 ft-lb/in? | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 1.00 J/cm? | 4.76 ft-lb/in? | Edgew 80*10*3 sp=62mm; ISO 179/1eA | |
| 1.50 J/cm? | 7.14 ft-lb/in? | ISO 179/2C | |
| 0.900 J/cm? @Temperature -30.0 °C | 4.28 ft-lb/in? @Temperature -22.0 °F | Edgew 80*10*3 sp=62mm; ISO 179/1eA | |
| Dart Drop, Total Energy | 61.0 J | 45.0 ft-lb | ASTM D3763 |
| Taber Abrasion, mg/1000 Cycles | 11 | 11 | CS-17, 1 kg; SABIC method |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 |
| Dielectric Constant | 2.8 @Frequency 1.00e+6 Hz | 2.8 @Frequency 1.00e+6 Hz | IEC 60250 |
| 2.9 @Frequency 50.0 - 60.0 Hz | 2.9 @Frequency 50.0 - 60.0 Hz | IEC 60250 | |
| Dielectric Strength | 16.0 kV/mm @Thickness 3.20 mm | 406 kV/in @Thickness 0.126 in | in oil; IEC 60243-1 |
| 25.0 kV/mm @Thickness 1.60 mm | 635 kV/in @Thickness 0.0630 in | in oil; IEC 60243-1 | |
| 33.0 kV/mm @Thickness 0.800 mm | 838 kV/in @Thickness 0.0315 in | in oil; IEC 60243-1 | |
| Dissipation Factor | 0.0010 @Frequency 50.0 - 60.0 Hz | 0.0010 @Frequency 50.0 - 60.0 Hz | IEC 60250 |
| 0.010 @Frequency 1.00e+6 Hz | 0.010 @Frequency 1.00e+6 Hz | IEC 60250 | |
| Comparative Tracking Index | 175 V | 175 V | IEC 60112 |
| 175 - 250 V | 175 - 250 V | UL 746A | |
| Hot Wire Ignition, HWI | 30 - 60 sec | 30 - 60 sec | UL 746A |
| High Amp Arc Ignition, HAI | 15 - 30 arcs | 15 - 30 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | 80.0 - 150 mm/min | 3.15 - 5.91 in/min | UL 746A |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 40.0 ?m/m-°C @Temperature 23.0 - 80.0 °C | 22.2 ?in/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 |
| 46.8 ?m/m-°C @Temperature -40.0 - 40.0 °C | 26.0 ?in/in-°F @Temperature -40.0 - 104 °F | ASTM E831 | |
| CTE, linear, Transverse to Flow | 70.0 ?m/m-°C @Temperature 23.0 - 80.0 °C | 38.9 ?in/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 |
| 84.6 ?m/m-°C @Temperature -40.0 - 40.0 °C | 47.0 ?in/in-°F @Temperature -40.0 - 104 °F | ASTM E831 | |
| Specific Heat Capacity | 1.21 J/g-°C | 0.289 BTU/lb-°F | ASTM C 351 |
| Thermal Conductivity | 0.200 W/m-K | 1.39 BTU-in/hr-ft?-°F | ASTM C177 |
| 0.210 W/m-K | 1.46 BTU-in/hr-ft?-°F | ISO 8302 | |
| Hot Ball Pressure Test | 125 °C | 257 °F | IEC 60695-10-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C | 288 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 144 °C | 291 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be | |
| 143 °C @Thickness 3.20 mm | 289 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 136 °C | 277 °F | 1.8 MPa Edgew 120*10*4 sp=100mm; ISO 75/Ae | |
| 138 °C @Thickness 3.20 mm | 280 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| 136 °C @Treatment Temp. 120 °C, Time 7200 sec | 277 °F @Treatment Temp. 248 °F, Time 2.00 hour | annealed; ISO 75/Ae | |
| Vicat Softening Point | 141 °C | 286 °F | Rate B/50; ISO 306 |
| 143 °C | 289 °F | Rate B/120; ISO 306 | |
| 149 °C | 300 °F | Rate B/50; ASTM D1525 | |
| UL RTI, Electrical | 130 °C | 266 °F | UL 746B |
| UL RTI, Mechanical with Impact | 130 °C | 266 °F | UL 746B |
| UL RTI, Mechanical without Impact | 130 °C | 266 °F | UL 746B |
| Flammability, UL94 | V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | UL 94 |
| 5VB @Thickness 2.00 mm | 5VB @Thickness 0.0787 in | UL 94 by SABIC-IP | |
| 5VA @Thickness 3.00 mm | 5VA @Thickness 0.118 in | UL 94 | |
| Oxygen Index | 37 % | 37 % | ISO 4589 |
| Glow Wire Test | 825 °C @Thickness 1.00 mm | 1520 °F @Thickness 0.0394 in | IEC 60695-2-13 |
| 960 °C @Thickness 1.00 mm | 1760 °F @Thickness 0.0394 in | IEC 60695-2-12 | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Hopper Temperature |
| Nozzle Temperature | 280 - 310 °C | 536 - 590 °F | Injection Molding |
| Zone 1 | 270 - 300 °C | 518 - 572 °F | |
| Zone 2 | 280 - 310 °C | 536 - 590 °F | |
| Zone 3 | 290 - 320 °C | 554 - 608 °F | |
| Melt Temperature | 290 - 320 °C | 554 - 608 °F | |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | |
| Drying Temperature | 120 °C | 248 °F | Injection Molding |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | Injection Molding |
| Moisture Content | 0.020 % | 0.020 % |