| 是否进口：否 | 产地：美国 | 厂家(产地)：沙伯基础(原GE) |
| 牌号：FR FL905 | 销售方式：品牌经销 | 类型：标准料 |
| 加工级别：注塑级 | 特性级别：阻燃级、 标准级 | 用途级别：汽车部件、 电子电器部件、 运动器材、 家电部件、 电动工具配件 |
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Density | 1.20 g/cc | 0.0434 lb/in? | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm @Thickness 3.20 mm | 0.0060 in/in @Thickness 0.126 in | SABIC method |
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm @Thickness 3.20 mm | 0.0050 in/in @Thickness 0.126 in | SABIC method |
| Melt Flow | 3.0 g/10 min @Load 1.20 kg, Temperature 300 °C | 3.0 g/10 min @Load 2.65 lb, Temperature 572 °F | cm?/10 min; ISO 1133 |
| 3.2 g/10 min @Load 1.20 kg, Temperature 300 °C | 3.2 g/10 min @Load 2.65 lb, Temperature 572 °F | ASTM D1238 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 44.0 MPa | 6380 psi | 50 mm/min; ISO 527 |
| 47.0 MPa | 6820 psi | 50 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 57.0 MPa | 8270 psi | 50 mm/min; ISO 527 |
| 58.0 MPa | 8410 psi | 50 mm/min; ASTM D638 | |
| Elongation at Break | 25 % | 25 % | 50 mm/min; ISO 527 |
| 30 % | 30 % | 50 mm/min; ASTM D638 | |
| Elongation at Yield | 5.7 % | 5.7 % | 50 mm/min; ASTM D638 |
| 5.9 % | 5.9 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 2.79 GPa | 405 ksi | 1mm/min; ISO 527 |
| 2.81 GPa | 408 ksi | 50 mm/min; ASTM D638 | |
| Flexural Yield Strength | 91.0 MPa | 13200 psi | 2 mm/min; ISO 178 |
| 98.0 MPa | 14200 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 2.67 GPa | 387 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 2.68 GPa | 389 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 5.20 J/cm | 9.74 ft-lb/in | ASTM D256 |
| 1.37 J/cm @Temperature -30.0 °C | 2.57 ft-lb/in @Temperature -22.0 °F | ASTM D256 | |
| Izod Impact, Notched (ISO) | 27.0 kJ/m? | 12.8 ft-lb/in? | 80*10*3; ISO 180/1A |
| 12.0 kJ/m? @Temperature -30.0 °C | 5.71 ft-lb/in? @Temperature -22.0 °F | 80*10*3; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 171 kJ/m? | 81.4 ft-lb/in? | 80*10*3; ISO 180/1U |
| 172 kJ/m? @Temperature -30.0 °C | 81.8 ft-lb/in? @Temperature -22.0 °F | 80*10*3; ISO 180/1U | |
| Charpy Impact Unnotched | 33.5 J/cm? | 159 ft-lb/in? | Edgew 80*10*3 sp=62mm; ISO 179/1eU |
| 31.3 J/cm? @Temperature -30.0 °C | 149 ft-lb/in? @Temperature -22.0 °F | Edgew 80*10*3 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 3.10 J/cm? | 14.8 ft-lb/in? | Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| 1.60 J/cm? @Temperature -30.0 °C | 7.61 ft-lb/in? @Temperature -22.0 °F | Edgew 80*10*3 sp=62mm; ISO 179/1eA | |
| Dart Drop, Total Energy | 53.0 J | 39.1 ft-lb | ASTM D3763 |
| 46.0 J @Temperature -30.0 °C | 33.9 ft-lb @Temperature -22.0 °F | ASTM D3763 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 52.0 ?m/m-°C @Temperature 23.0 - 80.0 °C | 28.9 ?in/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 |
| 54.0 ?m/m-°C @Temperature -40.0 - 95.0 °C | 30.0 ?in/in-°F @Temperature -40.0 - 203 °F | ASTM E831 | |
| CTE, linear, Transverse to Flow | 76.0 ?m/m-°C @Temperature 23.0 - 80.0 °C | 42.2 ?in/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 |
| 80.0 ?m/m-°C @Temperature -40.0 - 95.0 °C | 44.4 ?in/in-°F @Temperature -40.0 - 203 °F | ASTM E831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 145 °C | 293 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 146 °C @Thickness 3.20 mm | 295 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 134 °C | 273 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 140 °C @Thickness 3.20 mm | 284 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Vicat Softening Point | 147 °C | 297 °F | Rate B/50; ISO 306 |
| 148 °C | 298 °F | Rate A/50; ASTM D1525 | |
| 149 °C | 300 °F | Rate B/120; ISO 306 | |
| Flammability, UL94 | V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | UL 94 |
| 5VA @Thickness 6.00 mm | 5VA @Thickness 0.236 in | UL 94 | |
| Processing Properties | Metric | English | Comments |
| Nozzle Temperature | 290 - 310 °C | 554 - 590 °F | Injection Molding |
| Zone 1 | 270 - 295 °C | 518 - 563 °F | |
| Zone 2 | 280 - 305 °C | 536 - 581 °F | |
| Zone 3 | 295 - 315 °C | 563 - 599 °F | |
| Melt Temperature | 295 - 315 °C | 563 - 599 °F | |
| Mold Temperature | 70.0 - 95.0 °C | 158 - 203 °F | |
| Drying Temperature | 120 °C | 248 °F | Injection Molding |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Injection Molding |
| 48.0 hour | 48.0 hour | Cumulative; Injection Molding | |
| Moisture Content | 0.020 % | 0.020 % | |
| Back Pressure | 0.300 - 0.700 MPa | 43.5 - 102 psi | |
| Shot Size | 40 - 60 % | 40 - 60 % | |
| Vent Depth | 0.00250 - 0.00760 cm | 0.000984 - 0.00299 in | |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm | |
| Descriptive Properties | |||
| FOAM - Flame Class Minimum Density | 0.9 g/cm? |