| 是否进口：否 | 产地：美国 | 厂家(产地)：沙伯基础(原GE) |
| 牌号：FR LUX7169 | 销售方式：品牌经销 | 类型：标准料 |
| 加工级别：注塑级 | 特性级别：标准级 | 用途级别：汽车部件、 电子电器部件、 运动器材、 家电部件、 电动工具配件 |
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.38 g/cc | 1.38 g/cc | ASTM D792 |
| Density | 1.38 g/cc | 0.0499 lb/in? | ISO 1183 |
| Water Absorption | 0.35 % | 0.35 % | 23°C/sat; ISO 62 |
| Moisture Absorption | 0.150 % | 0.150 % | 23°C / 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm | 0.0050 - 0.0070 in/in @Thickness 0.126 in | SABIC method |
| Melt Flow | 22 g/10 min @Load 1.20 kg, Temperature 300 °C | 22 g/10 min @Load 2.65 lb, Temperature 572 °F | cm?/10 min; ISO 1133 |
| 22 g/10 min @Load 1.20 kg, Temperature 300 °C | 22 g/10 min @Load 2.65 lb, Temperature 572 °F | ASTM D1238 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 45.0 MPa | 6530 psi | 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 11 % | 11 % | 50 mm/min; ASTM D638 |
| Tensile Modulus | 2.80 GPa | 406 ksi | 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 85.0 MPa | 12300 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.60 GPa | 377 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 0.900 J/cm | 1.69 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 75.0 ?m/m-°C @Temperature -40.0 - 40.0 °C | 41.7 ?in/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 |
| 75.0 ?m/m-°C @Temperature -40.0 - 40.0 °C | 41.7 ?in/in-°F @Temperature -40.0 - 104 °F | ASTM E831 | |
| CTE, linear, Transverse to Flow | 75.0 ?m/m-°C @Temperature -40.0 - 40.0 °C | 41.7 ?in/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 |
| 75.0 ?m/m-°C @Temperature -40.0 - 40.0 °C | 41.7 ?in/in-°F @Temperature -40.0 - 104 °F | ASTM E831 | |
| Hot Ball Pressure Test | 135 °C | 275 °F | IEC 60695-10-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C | 266 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 134 °C @Thickness 6.40 mm | 273 °F @Thickness 0.252 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C | 239 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 115 °C @Thickness 3.20 mm | 239 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| 124 °C @Thickness 6.40 mm | 255 °F @Thickness 0.252 in | unannealed; ASTM D648 | |
| Vicat Softening Point | 142 °C | 288 °F | Rate B/50; ASTM D1525 |
| 143 °C | 289 °F | Rate B/120; ISO 306 | |
| Flammability, UL94 | V-0 @Thickness 0.900 mm | V-0 @Thickness 0.0354 in | UL 94 |
| Processing Properties | Metric | English | Comments |
| Nozzle Temperature | 265 - 290 °C | 509 - 554 °F | Injection Molding |
| Zone 1 | 250 - 270 °C | 482 - 518 °F | |
| Zone 2 | 260 - 280 °C | 500 - 536 °F | |
| Zone 3 | 270 - 295 °C | 518 - 563 °F | |
| Melt Temperature | 270 - 295 °C | 518 - 563 °F | |
| Mold Temperature | 70.0 - 95.0 °C | 158 - 203 °F | |
| Drying Temperature | 120 °C | 248 °F | Injection Molding |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Injection Molding |
| 48.0 hour | 48.0 hour | Cumulative; Injection Molding | |
| Moisture Content | 0.020 % | 0.020 % | |
| Back Pressure | 0.300 - 0.700 MPa | 43.5 - 102 psi | |
| Shot Size | 40 - 60 % | 40 - 60 % | |
| Vent Depth | 0.00250 - 0.00760 cm | 0.000984 - 0.00299 in | |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm |