| 是否进口：否 | 产地：美国 | 厂家(产地)：沙伯基础(原GE) |
| 牌号：FR 505RU | 销售方式：品牌经销 | 类型：标准料 |
| 加工级别：注塑级 | 特性级别：阻燃级、 标准级 | 用途级别：汽车部件、 电子电器部件、 运动器材、 家电部件、 电动工具配件 |
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.26 g/cc | 1.26 g/cc | ASTM D792 |
| Density | 1.26 g/cc | 0.0455 lb/in? | ISO 1183 |
| Water Absorption | 0.30 % | 0.30 % | 23°C/sat; ISO 62 |
| Moisture Absorption | 0.150 % | 0.150 % | 23°C / 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm | 0.0040 - 0.0060 in/in @Thickness 0.126 in | SABIC method |
| Melt Flow | 7.0 g/10 min @Load 1.20 kg, Temperature 300 °C | 7.0 g/10 min @Load 2.65 lb, Temperature 572 °F | cm?/10 min; ISO 1133 |
| 8.0 g/10 min @Load 1.20 kg, Temperature 300 °C | 8.0 g/10 min @Load 2.65 lb, Temperature 572 °F | ASTM D1238 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 60.0 MPa | 8700 psi | 5 mm/min; ISO 527 |
| 62.0 MPa | 8990 psi | 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 72.0 MPa | 10400 psi | 5 mm/min; ISO 527 |
| 74.0 MPa | 10700 psi | 5 mm/min; ASTM D638 | |
| Elongation at Break | 6.0 % | 6.0 % | 5 mm/min; ASTM D638 |
| 6.0 % | 6.0 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 3.0 % | 3.0 % | 5 mm/min; ISO 527 |
| 4.0 % | 4.0 % | 5 mm/min; ASTM D638 | |
| Tensile Modulus | 3.50 GPa | 508 ksi | 1mm/min; ISO 527 |
| 3.60 GPa | 522 ksi | 5 mm/min; ASTM D638 | |
| Flexural Yield Strength | 114 MPa | 16500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 122 MPa | 17700 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 3.20 GPa | 464 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 3.50 GPa | 508 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.900 J/cm | 1.69 ft-lb/in | ASTM D256 |
| 0.700 J/cm @Temperature -30.0 °C | 1.31 ft-lb/in @Temperature -22.0 °F | ASTM D256 | |
| Izod Impact, Unnotched | 12.0 J/cm | 22.5 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m? | 4.76 ft-lb/in? | 80*10*3; ISO 180/1A |
| 8.00 kJ/m? @Temperature -30.0 °C | 3.81 ft-lb/in? @Temperature -22.0 °F | 80*10*3; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB | NB | 80*10*3; ISO 180/1U |
| 73.0 kJ/m? @Temperature -30.0 °C | 34.7 ft-lb/in? @Temperature -22.0 °F | 80*10*3; ISO 180/1U | |
| Charpy Impact Unnotched | NB | NB | Edgew 80*10*3 sp=62mm; ISO 179/1eU |
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | Edgew 80*10*3 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 1.00 J/cm? | 4.76 ft-lb/in? | Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| 0.700 J/cm? @Temperature -30.0 °C | 3.33 ft-lb/in? @Temperature -22.0 °F | Edgew 80*10*3 sp=62mm; ISO 179/1eA | |
| Dart Drop, Total Energy | 25.0 J | 18.4 ft-lb | ASTM D3763 |
| Electrical Properties | Metric | English | Comments |
| Comparative Tracking Index | 175 V | 175 V | IEC 60112 |
| 175 - 250 V | 175 - 250 V | UL 746A | |
| Hot Wire Ignition, HWI | 15 - 30 sec | 15 - 30 sec | UL 746A |
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | UL 746A |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 50.0 ?m/m-°C @Temperature -40.0 - 40.0 °C | 27.8 ?in/in-°F @Temperature -40.0 - 104 °F | ASTM E831 |
| 50.0 ?m/m-°C @Temperature -40.0 - 40.0 °C | 27.8 ?in/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 74.0 ?m/m-°C @Temperature -40.0 - 40.0 °C | 41.1 ?in/in-°F @Temperature -40.0 - 104 °F | ASTM E831 |
| 85.0 ?m/m-°C @Temperature -40.0 - 40.0 °C | 47.2 ?in/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| Hot Ball Pressure Test | 125 °C | 257 °F | IEC 60695-10-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 136 °C | 277 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 137 °C @Thickness 3.20 mm | 279 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Vicat Softening Point | 147 °C | 297 °F | Rate B/50; ISO 306 |
| 149 °C | 300 °F | Rate B/50; ASTM D1525 | |
| 149 °C | 300 °F | Rate B/120; ISO 306 | |
| Flammability, UL94 | V-2 @Thickness 0.750 mm | V-2 @Thickness 0.0295 in | UL 94 by SABIC-IP |
| V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | UL 94 by SABIC-IP | |
| 5VB @Thickness 3.00 mm | 5VB @Thickness 0.118 in | UL 94 by SABIC-IP | |
| 5VA @Thickness 3.00 mm | 5VA @Thickness 0.118 in | UL 94 by SABIC-IP | |
| Glow Wire Test | 850 °C @Thickness 1.00 mm | 1560 °F @Thickness 0.0394 in | IEC 60695-2-13 |
| 875 °C @Thickness 3.00 mm | 1610 °F @Thickness 0.118 in | IEC 60695-2-13 | |
| 960 °C @Thickness 0.750 mm | 1760 °F @Thickness 0.0295 in | IEC 60695-2-12 | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Hopper Temperature |
| Nozzle Temperature | 280 - 310 °C | 536 - 590 °F | Injection Molding |
| Zone 1 | 270 - 300 °C | 518 - 572 °F | |
| Zone 2 | 280 - 310 °C | 536 - 590 °F | |
| Zone 3 | 290 - 320 °C | 554 - 608 °F | |
| Melt Temperature | 290 - 320 °C | 554 - 608 °F | |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | |
| Drying Temperature | 120 °C | 248 °F | Injection Molding |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | Injection Molding |
| Moisture Content | 0.020 % | 0.020 % | |
| Descriptive Properties | |||
| UV-light, water exposure/immersion | F1 | UL 746C |
本公司长期销售沙伯基础 PC，ABS，ASA，EVA，PA6，PBT，PE，PBT，PET，PMMA，POM，PS，PP，PU，PES，PEI料等多种牌号
我司产品均可提供详细物性表(英文和中文版)相关资料；可开13%增值税发票；免费为客户分析样版并提供原料型号咨询服务(可免费帮客户翻译英文资料)；如需试料、了解产品相关信息及当日报价，敬请来电、竭诚为您服务！