| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Density | 1.20 g/cc | 0.0434 lb/in? | ASTM D792 |
| 1.20 g/cc | 0.0434 lb/in? | ISO 1183 | |
| Moisture Absorption | 0.150 % | 0.150 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.30 % | 0.30 % | ISO 62-1 |
| Viscosity | 51 cP @Load 1.20 kg, Temperature 300 °C | 51 cP @Load 2.65 lb, Temperature 572 °F | MVR cc/10 min; ISO 1133 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm | 0.0050 - 0.0070 in/in @Thickness 0.126 in | SABIC method |
| Melt Flow | 55 g/10 min @Load 1.20 kg, Temperature 300 °C | 55 g/10 min @Load 2.65 lb, Temperature 572 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength at Break | 56.0 MPa | 8120 psi | 50 mm/min; ISO 527 |
| 57.0 MPa | 8270 psi | 50 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | 50 mm/min; ASTM D638 |
| 61.0 MPa | 8850 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 100 % | 100 % | 50 mm/min; ISO 527 |
| 114 % | 114 % | 50 mm/min; ASTM D638 | |
| Elongation at Yield | 5.5 % | 5.5 % | 50 mm/min; ASTM D638 |
| 6.0 % | 6.0 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 2.20 GPa | 319 ksi | 1 mm/min; ISO 527 |
| 2.30 GPa | 334 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 90.0 MPa | 13100 psi | yield, 2 mm/min; ISO 178 |
| 100 MPa | 14500 psi | yld, 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 2.20 GPa | 319 ksi | 2 mm/min; ISO 178 |
| 2.28 GPa | 331 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact Notched | 674 J | 497 ft-lb | ASTM D256 |
| 108 J @Temperature -30.0 °C | 79.7 ft-lb @Temperature -22.0 °F | ASTM D256 | |
| 325 J @Temperature 0.000 °C | 240 ft-lb @Temperature 32.0 °F | ASTM D256 | |
| Izod Impact, Notched (ISO) | 55.0 kJ/m? | 26.2 ft-lb/in? | 80*10*3; ISO 180/1A |
| 10.0 kJ/m? @Temperature -30.0 °C | 4.76 ft-lb/in? @Temperature -22.0 °F | 80*10*3; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB | NB | 80*10*3; ISO 180/1U |
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | 80*10*3; ISO 180/1U | |
| Charpy Impact Unnotched | NB | NB | Edgew 80*10*3 sp=62mm; ISO 179/1eU |
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | Edgew 80*10*3 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 6.00 J/cm? | 28.6 ft-lb/in? | Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| 1.10 J/cm? @Temperature -30.0 °C | 5.23 ft-lb/in? @Temperature -22.0 °F | Edgew 80*10*3 sp=62mm; ISO 179/1eA | |
| Dart Drop, Total Energy | 56.0 J | 41.3 ft-lb | ASTM D3763 |
| Impact Test | 92.0 J | 67.9 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 80.0 ?m/m-°C @Temperature -40.0 - 40.0 °C | 44.4 ?in/in-°F @Temperature -40.0 - 104 °F | ASTM E831 |
| 80.0 ?m/m-°C @Temperature -40.0 - 40.0 °C | 44.4 ?in/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 80.0 ?m/m-°C @Temperature -40.0 - 40.0 °C | 44.4 ?in/in-°F @Temperature -40.0 - 104 °F | ASTM E831 |
| 80.0 ?m/m-°C @Temperature -40.0 - 40.0 °C | 44.4 ?in/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| Hot Ball Pressure Test | 125 °C | 257 °F | PASS; IEC 60695-10-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C @Thickness 3.20 mm | 255 °F @Thickness 0.126 in | unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 110 °C @Thickness 3.20 mm | 230 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Vicat Softening Point | 135 °C | 275 °F | Rate B/50; ISO 306 |
| 136 °C | 277 °F | Rate B/120; ISO 306 | |
| 141 °C | 286 °F | Rate B/50; ASTM D1525 | |
| UL RTI, Electrical | 115 °C | 239 °F | UL 746B |
| UL RTI, Mechanical with Impact | 105 °C | 221 °F | UL 746B |
| UL RTI, Mechanical without Impact | 115 °C | 239 °F | UL 746B |
| Flammability, UL94 | HB @Thickness >=0.500 mm | HB @Thickness >=0.0197 in | UL 94 |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.582 | 1.582 | ASTM D542 |
| Haze | <= 1.0 % @Thickness 2.54 mm | <= 1.0 % @Thickness 0.100 in | ASTM D1003 |
| Transmission, Visible | 88 % @Thickness 2.54 mm | 88 % @Thickness 0.100 in | ASTM D1003 |
| Processing Properties | Metric | English | Comments |
| Nozzle Temperature | 255 - 300 °C | 491 - 572 °F | |
| Zone 2 | 250 - 295 °C | 482 - 563 °F | |
| Zone 3 | 260 - 305 °C | 500 - 581 °F | |
| Melt Temperature | 260 - 305 °C | 500 - 581 °F | Injection Molding |
| Mold Temperature | 50.0 - 80.0 °C | 122 - 176 °F | |
| Drying Temperature | 105 - 110 °C | 221 - 230 °F | Injection Molding |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Injection Molding |
| 24.0 hour | 24.0 hour | Cumulative; Injection Molding | |
| Back Pressure | 0.300 - 0.700 MPa | 43.5 - 102 psi | |
| Shot Size | 40 - 60 % | 40 - 60 % | |
| Vent Depth | 0.00380 - 0.00760 cm | 0.00150 - 0.00299 in | |
| Screw Speed | 35 - 75 rpm | 35 - 75 rpm |