是否进口:否 | 产地:美国 | 厂家(产地):沙伯基础(原GE) |
牌号:153R | 销售方式:品牌经销 | 类型:标准料 |
加工级别:注塑级 | 特性级别:标准级 | 用途级别:汽车部件、 电子电器部件、 运动器材、 家电部件、 电动工具配件 |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
1.20 g/cc | 1.20 g/cc | ASTM D792 | |
Density | 1.19 g/cc | 0.0430 lb/in? | ASTM D792 |
Water Absorption | 0.15 % | 0.15 % | 24 hours; ASTM D570 |
Moisture Absorption at Equilibrium | 0.35 % | 0.35 % | ASTM D570 |
0.58 % @Temperature 100 °C | 0.58 % @Temperature 212 °F | ASTM D570 | |
Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm | 0.0050 - 0.0070 in/in @Thickness 0.126 in | SABIC method |
Melt Flow | 2.5 g/10 min @Load 1.20 kg, Temperature 300 °C | 2.5 g/10 min @Load 2.65 lb, Temperature 572 °F | ASTM D1238 |
Mechanical Properties | Metric | English | Comments |
Hardness, Rockwell M | 70 | 70 | ASTM D785 |
Hardness, Rockwell R | 118 | 118 | ASTM D785 |
Tensile Strength at Break | 65.0 MPa | 9430 psi | 50 mm/min; ASTM D638 |
Tensile Strength, Yield | 62.0 MPa | 8990 psi | 50 mm/min; ASTM D638 |
Elongation at Break | 110 % | 110 % | 50 mm/min; ASTM D638 |
Elongation at Yield | 7.0 % | 7.0 % | 50 mm/min; ASTM D638 |
Flexural Yield Strength | 93.0 MPa | 13500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
Flexural Modulus | 2.34 GPa | 339 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
Izod Impact, Notched | 7.47 J/cm | 14.0 ft-lb/in | ASTM D256 |
Izod Impact, Unnotched | 32.04 J/cm | 60.02 ft-lb/in | ASTM D4812 |
Tensile Impact Strength | 630 kJ/m? | 300 ft-lb/in? | ASTM D1822 |
Falling Dart Impact | 169 J | 125 ft-lb | ASTM D3029 |
Taber Abrasion, mg/1000 Cycles | 10 | 10 | CS-17, 1 kg; ASTM D1044 |
Electrical Properties | Metric | English | Comments |
Volume Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | ASTM D257 |
Dielectric Constant | 2.96 @Frequency 1.00e+6 Hz | 2.96 @Frequency 1.00e+6 Hz | ASTM D150 |
3.17 @Frequency 50.0 - 60.0 Hz | 3.17 @Frequency 50.0 - 60.0 Hz | ASTM D150 | |
Dielectric Strength | 14.9 kV/mm @Thickness 3.20 mm | 378 kV/in @Thickness 0.126 in | in air; ASTM D149 |
Dissipation Factor | 0.00090 @Frequency 50.0 - 60.0 Hz | 0.00090 @Frequency 50.0 - 60.0 Hz | ASTM D150 |
0.010 @Frequency 1.00e+6 Hz | 0.010 @Frequency 1.00e+6 Hz | ASTM D150 | |
Thermal Properties | Metric | English | Comments |
CTE, linear, Parallel to Flow | 68.4 ?m/m-°C @Temperature -40.0 - 95.0 °C | 38.0 ?in/in-°F @Temperature -40.0 - 203 °F | ASTM E831 |
Specific Heat Capacity | 1.25 J/g-°C | 0.299 BTU/lb-°F | ASTM C 351 |
Thermal Conductivity | 0.190 W/m-K | 1.32 BTU-in/hr-ft?-°F | ASTM C177 |
Deflection Temperature at 0.46 MPa (66 psi) | 137 °C @Thickness 6.40 mm | 279 °F @Thickness 0.252 in | unannealed; ASTM D648 |
Deflection Temperature at 1.8 MPa (264 psi) | 132 °C @Thickness 6.40 mm | 270 °F @Thickness 0.252 in | unannealed; ASTM D648 |
Vicat Softening Point | 157 °C | 315 °F | Rate B/50; ASTM D1525 |
Optical Properties | Metric | English | Comments |
Refractive Index | 1.586 | 1.586 | ASTM D542 |
Haze | 1.0 % @Thickness 2.54 mm | 1.0 % @Thickness 0.100 in | ASTM D1003 |
Transmission, Visible | 88 % @Thickness 2.54 mm | 88 % @Thickness 0.100 in | ASTM D1003 |
Processing Properties | Metric | English | Comments |
Nozzle Temperature | 315 - 340 °C | 599 - 644 °F | Injection Molding |
Zone 1 | 260 - 290 °C | 500 - 554 °F | Extrusion Blow Molding |
300 - 320 °C | 572 - 608 °F | ||
Zone 2 | 260 - 290 °C | 500 - 554 °F | Extrusion Blow Molding |
310 - 330 °C | 590 - 626 °F | ||
Zone 3 | 260 - 290 °C | 500 - 554 °F | Extrusion Blow Molding |
320 - 345 °C | 608 - 653 °F | ||
Zone 4 | 260 - 290 °C | 500 - 554 °F | Extrusion Blow Molding |
Zone 5 | 260 - 290 °C | 500 - 554 °F | |
Melt Temperature | 265 - 280 °C | 509 - 536 °F | |
320 - 345 °C | 608 - 653 °F | ||
Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | |
80.0 - 115 °C | 176 - 239 °F | ||
Drying Temperature | 120 °C | 248 °F | Extrusion Blow Molding |
120 °C | 248 °F | Injection Molding | |
Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | Extrusion Blow Molding |
3.00 - 4.00 hour | 3.00 - 4.00 hour | Injection Molding | |
48.0 hour | 48.0 hour | Cumulative; Injection Molding | |
Moisture Content | >= 0.010 % | >= 0.010 % | |
0.020 % | 0.020 % | ||
0.020 % | 0.020 % | ||
Back Pressure | 0.300 - 0.700 MPa | 43.5 - 102 psi | |
Shot Size | 40 - 60 % | 40 - 60 % | |
Vent Depth | 0.00250 - 0.00760 cm | 0.000984 - 0.00299 in | |
Screw Speed | 40 - 70 rpm | 40 - 70 rpm |