是否进口:否 | 产地:美国 | 厂家(产地):沙伯基础(原GE) |
牌号:144R | 销售方式:品牌经销 | 类型:标准料 |
加工级别:注塑级 | 特性级别:标准级 | 用途级别:汽车部件、 电子电器部件、 运动器材、 家电部件、 电动工具配件 |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
1.20 g/cc | 1.20 g/cc | ASTM D792 | |
Density | 1.19 g/cc | 0.0430 lb/in? | ASTM D792 |
Water Absorption | 0.15 % | 0.15 % | 24 hours; ASTM D570 |
Moisture Absorption at Equilibrium | 0.35 % | 0.35 % | ASTM D570 |
0.58 % @Temperature 100 °C | 0.58 % @Temperature 212 °F | ASTM D570 | |
Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm | 0.0050 - 0.0070 in/in @Thickness 0.126 in | SABIC method |
Melt Flow | 10.5 g/10 min @Load 1.20 kg, Temperature 300 °C | 10.5 g/10 min @Load 2.65 lb, Temperature 572 °F | ASTM D1238 |
12 g/10 min @Load 1.20 kg, Temperature 300 °C | 12 g/10 min @Load 2.65 lb, Temperature 572 °F | cm?/10 min; ISO 1133 | |
Mechanical Properties | Metric | English | Comments |
Hardness, Rockwell M | 70 | 70 | ASTM D785 |
Hardness, Rockwell R | 118 | 118 | ASTM D785 |
Tensile Strength at Break | 68.0 MPa | 9860 psi | 50 mm/min; ASTM D638 |
70.0 MPa | 10200 psi | 50 mm/min; ISO 527 | |
Tensile Strength, Yield | 62.0 MPa | 8990 psi | 50 mm/min; ASTM D638 |
63.0 MPa | 9140 psi | 50 mm/min; ISO 527 | |
Elongation at Break | 110 % | 110 % | 50 mm/min; ISO 527 |
130 % | 130 % | 50 mm/min; ASTM D638 | |
Elongation at Yield | 6.0 % | 6.0 % | 50 mm/min; ISO 527 |
7.0 % | 7.0 % | 50 mm/min; ASTM D638 | |
Tensile Modulus | 2.35 GPa | 341 ksi | 1mm/min; ISO 527 |
2.37 GPa | 344 ksi | 50 mm/min; ASTM D638 | |
Flexural Yield Strength | 90.0 MPa | 13100 psi | 2 mm/min; ISO 178 |
97.0 MPa | 14100 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
Flexural Modulus | 2.30 GPa | 334 ksi | 2 mm/min; ISO 178 |
2.34 GPa | 339 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
Izod Impact, Notched | 8.01 J/cm | 15.0 ft-lb/in | ASTM D256 |
8.01 J/cm | 15.0 ft-lb/in | colors; ASTM D256 | |
8.01 J/cm | 15.0 ft-lb/in | natural, tints; ASTM D256 | |
Izod Impact, Unnotched | 32.04 J/cm | 60.02 ft-lb/in | ASTM D4812 |
Izod Impact, Notched (ISO) | 12.0 kJ/m? | 5.71 ft-lb/in? | 80*10*4; ISO 180/1A |
10.0 kJ/m? @Temperature -30.0 °C | 4.76 ft-lb/in? @Temperature -22.0 °F | 80*10*4; ISO 180/1A | |
Izod Impact, Unnotched (ISO) | NB | NB | 80*10*4; ISO 180/1U |
NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | 80*10*4; ISO 180/1U | |
Charpy Impact Unnotched | NB | NB | Edgew 80*10*4 sp=62mm; ISO 179/1eU |
NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
Charpy Impact, Notched | 3.50 J/cm? | 16.7 ft-lb/in? | ISO 179/2C |
Tensile Impact Strength | 577 kJ/m? | 275 ft-lb/in? | ASTM D1822 |
Dart Drop, Total Energy | 63.0 J | 46.5 ft-lb | peak; ASTM D3763 |
Falling Dart Impact | 169 J | 125 ft-lb | ASTM D3029 |
Taber Abrasion, mg/1000 Cycles | 10 | 10 | CS-17, 1 kg; ASTM D1044 |
Electrical Properties | Metric | English | Comments |
Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
>= 1.00e+17 ohm-cm | >= 1.00e+17 ohm-cm | ASTM D257 | |
Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 |
Dielectric Constant | 2.7 @Frequency 1.00e+6 Hz | 2.7 @Frequency 1.00e+6 Hz | IEC 60250 |
2.7 @Frequency 50.0 - 60.0 Hz | 2.7 @Frequency 50.0 - 60.0 Hz | IEC 60250 | |
2.96 @Frequency 1.00e+6 Hz | 2.96 @Frequency 1.00e+6 Hz | ASTM D150 | |
3.17 @Frequency 50.0 - 60.0 Hz | 3.17 @Frequency 50.0 - 60.0 Hz | ASTM D150 | |
Dielectric Strength | 14.9 kV/mm @Thickness 3.20 mm | 378 kV/in @Thickness 0.126 in | in air; ASTM D149 |
17.0 kV/mm @Thickness 3.20 mm | 432 kV/in @Thickness 0.126 in | in oil; IEC 60243-1 | |
Dissipation Factor | 0.00090 @Frequency 50.0 - 60.0 Hz | 0.00090 @Frequency 50.0 - 60.0 Hz | ASTM D150 |
0.0010 @Frequency 50.0 - 60.0 Hz | 0.0010 @Frequency 50.0 - 60.0 Hz | IEC 60250 | |
0.010 @Frequency 1.00e+6 Hz | 0.010 @Frequency 1.00e+6 Hz | IEC 60250 | |
0.010 @Frequency 1.00e+6 Hz | 0.010 @Frequency 1.00e+6 Hz | ASTM D150 | |
Comparative Tracking Index | 250 - 400 V | 250 - 400 V | UL 746A |
Hot Wire Ignition, HWI | 30 - 60 sec | 30 - 60 sec | UL 746A |
High Amp Arc Ignition, HAI | 60 - 120 arcs | 60 - 120 arcs | UL 746A |
High Voltage Arc-Tracking Rate, HVTR | 25.4 - 80.0 mm/min | 1.00 - 3.15 in/min | UL 746A |
Thermal Properties | Metric | English | Comments |
CTE, linear, Parallel to Flow | 68.4 ?m/m-°C @Temperature -40.0 - 95.0 °C | 38.0 ?in/in-°F @Temperature -40.0 - 203 °F | ASTM E831 |
70.0 ?m/m-°C @Temperature 23.0 - 80.0 °C | 38.9 ?in/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 | |
Specific Heat Capacity | 1.25 J/g-°C | 0.299 BTU/lb-°F | ASTM C 351 |
Thermal Conductivity | 0.190 W/m-K | 1.32 BTU-in/hr-ft?-°F | ASTM C177 |
0.200 W/m-K | 1.39 BTU-in/hr-ft?-°F | ISO 8302 | |
Hot Ball Pressure Test | 125 °C | 257 °F | IEC 60695-10-2 |
Deflection Temperature at 0.46 MPa (66 psi) | 136 °C | 277 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
137 °C @Thickness 6.40 mm | 279 °F @Thickness 0.252 in | unannealed; ASTM D648 | |
Deflection Temperature at 1.8 MPa (264 psi) | 125 °C | 257 °F | 1.8 MPa Edgew 120*10*4 sp=100mm; ISO 75/Ae |
132 °C @Thickness 6.40 mm | 270 °F @Thickness 0.252 in | unannealed; ASTM D648 | |
Vicat Softening Point | 141 °C | 286 °F | Rate B/50; ISO 306 |
142 °C | 288 °F | Rate B/120; ISO 306 | |
153 °C | 307 °F | Rate A/50; ISO 306 | |
154 °C | 309 °F | Rate B/50; ASTM D1525 | |
UL RTI, Electrical | 130 °C | 266 °F | UL 746B |
UL RTI, Mechanical with Impact | 130 °C | 266 °F | UL 746B |
UL RTI, Mechanical without Impact | 130 °C | 266 °F | UL 746B |
Flammability, UL94 | HB @Thickness 1.47 mm | HB @Thickness 0.0579 in | UL 94 |
Oxygen Index | 25 % | 25 % | ASTM D2863 |
25 % | 25 % | ISO 4589 | |
Optical Properties | Metric | English | Comments |
Refractive Index | 1.586 | 1.586 | ASTM D542 |
Haze | 1.0 % @Thickness 2.54 mm | 1.0 % @Thickness 0.100 in | ASTM D1003 |
Transmission, Visible | 88 % @Thickness 2.54 mm | 88 % @Thickness 0.100 in | ASTM D1003 |
Processing Properties | Metric | English | Comments |
Nozzle Temperature | 290 - 310 °C | 554 - 590 °F | Injection Molding |
Zone 1 | 270 - 295 °C | 518 - 563 °F | |
Zone 2 | 280 - 305 °C | 536 - 581 °F | |
Zone 3 | 295 - 315 °C | 563 - 599 °F | |
Melt Temperature | 295 - 315 °C | 563 - 599 °F | |
Mold Temperature | 70.0 - 95.0 °C | 158 - 203 °F | |
Drying Temperature | 120 °C | 248 °F | Injection Molding |
Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Injection Molding |
48.0 hour | 48.0 hour | Cumulative; Injection Molding | |
Moisture Content | 0.020 % | 0.020 % | |
Back Pressure | 0.300 - 0.700 MPa | 43.5 - 102 psi | |
Shot Size | 40 - 60 % | 40 - 60 % | |
Vent Depth | 0.00250 - 0.00760 cm | 0.000984 - 0.00299 in | |
Screw Speed | 40 - 70 rpm | 40 - 70 rpm |