| 是否进口：否 | 产地：美国 | 厂家(产地)：沙伯基础(原GE) |
| 牌号：LUX1619 | 销售方式：品牌经销 | 类型：标准料 |
| 加工级别：注塑级、 挤出级 | 特性级别：标准级 | 用途级别：汽车部件、 电子电器部件、 运动器材、 家电部件、 电动工具配件 |
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.34 g/cc | 1.34 g/cc | ASTM D792 |
| Density | 1.34 g/cc | 0.0484 lb/in? | ISO 1183 |
| Water Absorption | 0.35 % | 0.35 % | 23°C/sat; ISO 62 |
| Moisture Absorption | 0.150 % | 0.150 % | 23°C / 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0080 - 0.010 cm/cm @Thickness 3.20 mm | 0.0080 - 0.010 in/in @Thickness 0.126 in | SABIC method |
| Melt Flow | 7.5 g/10 min @Load 1.20 kg, Temperature 300 °C | 7.5 g/10 min @Load 2.65 lb, Temperature 572 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 50.0 MPa | 7250 psi | 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 57.0 MPa | 8270 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 74 % | 74 % | 50 mm/min; ASTM D638 |
| Elongation at Yield | 6.0 % | 6.0 % | 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 97.0 MPa | 14100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.73 GPa | 396 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 6.40 J/cm | 12.0 ft-lb/in | ASTM D256 |
| 1.35 J/cm @Temperature -30.0 °C | 2.53 ft-lb/in @Temperature -22.0 °F | ASTM D256 | |
| Izod Impact, Unnotched | 21.3 J/cm | 39.9 ft-lb/in | ASTM D4812 |
| Dart Drop, Total Energy | 69.0 J | 50.9 ft-lb | ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 61.0 ?m/m-°C @Temperature -40.0 - 40.0 °C | 33.9 ?in/in-°F @Temperature -40.0 - 104 °F | ASTM E831 |
| CTE, linear, Transverse to Flow | 64.0 ?m/m-°C @Temperature -40.0 - 40.0 °C | 35.6 ?in/in-°F @Temperature -40.0 - 104 °F | ASTM E831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 141 °C @Thickness 3.20 mm | 286 °F @Thickness 0.126 in | unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 129 °C @Thickness 3.20 mm | 264 °F @Thickness 0.126 in | unannealed; ASTM D648 |
| Vicat Softening Point | 147 °C | 297 °F | Rate B/50; ASTM D1525 |
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | UL 94 |
| Glow Wire Test | 850 °C @Thickness 1.50 mm | 1560 °F @Thickness 0.0591 in | IEC 60695-2-13 |
| 850 °C @Thickness 3.00 mm | 1560 °F @Thickness 0.118 in | IEC 60695-2-13 | |
| 960 °C @Thickness 1.50 - 3.00 mm | 1760 °F @Thickness 0.0591 - 0.118 in | IEC 60695-2-12 | |
| Processing Properties | Metric | English | Comments |
| Nozzle Temperature | 305 - 325 °C | 581 - 617 °F | Injection Molding |
| Zone 1 | 290 - 310 °C | 554 - 590 °F | |
| Zone 2 | 300 - 320 °C | 572 - 608 °F | |
| Zone 3 | 310 - 330 °C | 590 - 626 °F | |
| Melt Temperature | 310 - 330 °C | 590 - 626 °F | |
| Mold Temperature | 80.0 - 115 °C | 176 - 239 °F | |
| Drying Temperature | 120 °C | 248 °F | Injection Molding |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Injection Molding |
| 48.0 hour | 48.0 hour | Cumulative; Injection Molding | |
| Moisture Content | 0.020 % | 0.020 % | |
| Back Pressure | 0.300 - 0.700 MPa | 43.5 - 102 psi | |
| Shot Size | 40 - 60 % | 40 - 60 % | |
| Vent Depth | 0.00250 - 0.00760 cm | 0.000984 - 0.00299 in | |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm |