| 是否进口：否 | 产地：美国 | 厂家(产地)：沙伯基础(原GE) |
| 牌号：133R | 销售方式：品牌经销 | 类型：标准料 |
| 加工级别：注塑级 | 特性级别：标准级 | 用途级别：汽车部件、 电子电器部件、 运动器材、 家电部件、 电动工具配件 |
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in? | ISO 1183 |
| Water Absorption | 0.35 % | 0.35 % | 23°C/sat; ISO 62 |
| Moisture Absorption | 0.150 % | 0.150 % | 23°C / 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | SABIC method |
| Melt Flow | 3.0 g/10 min @Load 1.20 kg, Temperature 300 °C | 3.0 g/10 min @Load 2.65 lb, Temperature 572 °F | cm?/10 min; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Ball Indentation Hardness | 95.0 MPa | 13800 psi | ISO 2039-1 |
| Tensile Strength at Break | 70.0 MPa | 10200 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 120 % | 120 % | 50 mm/min; ISO 527 |
| Elongation at Yield | 7.0 % | 7.0 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 2.35 GPa | 341 ksi | 1mm/min; ISO 527 |
| Flexural Yield Strength | 90.0 MPa | 13100 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.30 GPa | 334 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 75.0 kJ/m? | 35.7 ft-lb/in? | 80*10*3; ISO 180/1A |
| 13.0 kJ/m? @Temperature -30.0 °C | 6.19 ft-lb/in? @Temperature -22.0 °F | 80*10*3; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB | NB | 80*10*3; ISO 180/1U |
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | 80*10*3; ISO 180/1U | |
| Charpy Impact Unnotched | NB | NB | Edgew 80*10*3 sp=62mm; ISO 179/1eU |
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | Edgew 80*10*3 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 3.50 J/cm? | 16.7 ft-lb/in? | ISO 179/2C |
| 8.00 J/cm? | 38.1 ft-lb/in? | Edgew 80*10*3 sp=62mm; ISO 179/1eA | |
| 1.60 J/cm? @Temperature -30.0 °C | 7.61 ft-lb/in? @Temperature -22.0 °F | Edgew 80*10*3 sp=62mm; ISO 179/1eA | |
| Taber Abrasion, mg/1000 Cycles | 10 | 10 | CS-17, 1 kg; SABIC method |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 |
| Dielectric Constant | 2.7 @Frequency 50.0 - 60.0 Hz | 2.7 @Frequency 50.0 - 60.0 Hz | IEC 60250 |
| 2.7 @Frequency 1.00e+6 Hz | 2.7 @Frequency 1.00e+6 Hz | IEC 60250 | |
| Dielectric Strength | 16.5 kV/mm @Thickness 1.00 mm | 419 kV/in @Thickness 0.0394 in | shorttime; IEC 60243-1 |
| 17.0 kV/mm @Thickness 3.20 mm | 432 kV/in @Thickness 0.126 in | in oil; IEC 60243-1 | |
| Dissipation Factor | 0.0010 @Frequency 50.0 - 60.0 Hz | 0.0010 @Frequency 50.0 - 60.0 Hz | IEC 60250 |
| 0.010 @Frequency 1.00e+6 Hz | 0.010 @Frequency 1.00e+6 Hz | IEC 60250 | |
| Comparative Tracking Index | 250 V | 250 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 70.0 ?m/m-°C @Temperature 23.0 - 80.0 °C | 38.9 ?in/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 70.0 ?m/m-°C @Temperature -40.0 - 40.0 °C | 38.9 ?in/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 |
| Thermal Conductivity | 0.200 W/m-K | 1.39 BTU-in/hr-ft?-°F | ISO 8302 |
| Hot Ball Pressure Test | 125 °C | 257 °F | IEC 60695-10-2 |
| 140 °C | 284 °F | IEC 60695-10-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 139 °C | 282 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| Deflection Temperature at 1.8 MPa (264 psi) | 128 °C | 262 °F | 1.8 MPa Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| Vicat Softening Point | 144 °C | 291 °F | Rate B/50; ISO 306 |
| 145 °C | 293 °F | Rate B/120; ISO 306 | |
| Glow Wire Test | 850 °C @Thickness 1.00 mm | 1560 °F @Thickness 0.0394 in | IEC 60695-2-12 |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.586 | 1.586 | ISO 489 |
| Haze | <= 0.80 % @Thickness 2.54 mm | <= 0.80 % @Thickness 0.100 in | ASTM D1003 |
| Transmission, Visible | 88 - 90 % @Thickness 2.54 mm | 88 - 90 % @Thickness 0.100 in | ASTM D1003 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 40.0 - 60.0 °C | 104 - 140 °F | Hopper Temperature |
| Zone 1 | 260 - 280 °C | 500 - 536 °F | Profile Extrusion |
| Zone 2 | 260 - 280 °C | 500 - 536 °F | Profile Extrusion |
| Zone 3 | 260 - 280 °C | 500 - 536 °F | Profile Extrusion |
| Zone 4 | 260 - 280 °C | 500 - 536 °F | Profile Extrusion |
| Adapter Temperature | 260 - 280 °C | 500 - 536 °F | Profile Extrusion |
| Die Temperature | 250 - 260 °C | 482 - 500 °F | Profile Extrusion |
| Melt Temperature | 270 - 280 °C | 518 - 536 °F | |
| Drying Temperature | 120 °C | 248 °F | Profile Extrusion |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | Profile Extrusion |
| Precipitation Temperature | 70.0 - 90.0 °C | 158 - 194 °F | Calibrator |
本公司长期销售沙伯基础 PC，ABS，ASA，EVA，PA6，PBT，PE，PBT，PET，PMMA，POM，PS，PP，PU，PES，PEI料等多种牌号
我司产品均可提供详细物性表(英文和中文版)相关资料；可开13%增值税发票；免费为客户分析样版并提供原料型号咨询服务(可免费帮客户翻译英文资料)；如需试料、了解产品相关信息及当日报价，敬请来电、竭诚为您服务！