是否进口:否 | 产地:美国 | 厂家(产地):沙伯基础(原GE) |
牌号:HFD4471 | 销售方式:品牌经销 | 类型:标准料 |
加工级别:注塑级 | 特性级别:标准级 | 用途级别:汽车部件、 电子电器部件、 运动器材、 家电部件、 电动工具配件 |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Specific Gravity | 1.26 g/cc | 1.26 g/cc | ASTM D792 |
Density | 1.25 g/cc | 0.0452 lb/in? | ISO 1183 |
Moisture Absorption | 0.0200 % | 0.0200 % | Injection Molding |
0.0400 % | 0.0400 % | 23°C / 50% RH; ISO 62 | |
Water Absorption at Saturation | 0.14 % | 0.14 % | ISO 62-1 |
Viscosity | 9.0 cP @Load 1.20 kg, Temperature 300 °C | 9.0 cP @Load 2.65 lb, Temperature 572 °F | MVR cc/10 min; ISO 1133 |
Linear Mold Shrinkage, Flow | 0.0030 - 0.0040 cm/cm @Thickness 3.20 mm | 0.0030 - 0.0040 in/in @Thickness 0.126 in | SABIC method |
Linear Mold Shrinkage, Transverse | 0.0040 - 0.0050 cm/cm @Thickness 3.20 mm | 0.0040 - 0.0050 in/in @Thickness 0.126 in | SABIC method |
Melt Flow | 10 g/10 min @Load 1.20 kg, Temperature 300 °C | 10 g/10 min @Load 2.65 lb, Temperature 572 °F | ASTM D1238 |
Mechanical Properties | Metric | English | Comments |
Tensile Strength at Break | 37.0 MPa | 5370 psi | 5 mm/min; ASTM D638 |
41.0 MPa | 5950 psi | 5 mm/min; ISO 527 | |
Tensile Strength, Yield | 54.0 MPa | 7830 psi | 5 mm/min; ASTM D638 |
58.0 MPa | 8410 psi | 5 mm/min; ISO 527 | |
Elongation at Break | 10 % | 10 % | 5 mm/min; ISO 527 |
Elongation at Yield | 3.0 % | 3.0 % | 5 mm/min; ASTM D638 |
3.0 % | 3.0 % | 5 mm/min; ISO 527 | |
Tensile Modulus | 3.70 GPa | 537 ksi | 5 mm/min; ASTM D638 |
Flexural Strength | 95.0 MPa | 13800 psi | yld, 1.3 mm/min, 50 mm span; ASTM D790 |
Flexural Modulus | 3.30 GPa | 479 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
Izod Impact Notched | 290 J | 214 ft-lb | ASTM D256 |
Izod Impact, Unnotched | 21.0 J/cm | 39.3 ft-lb/in | ASTM D4812 |
Izod Impact, Notched (ISO) | 30.0 kJ/m? | 14.3 ft-lb/in? | 80*10*3; ISO 180/1A |
13.0 kJ/m? @Temperature -30.0 °C | 6.19 ft-lb/in? @Temperature -22.0 °F | 80*10*3; ISO 180/1A | |
Izod Impact, Unnotched (ISO) | 175 kJ/m? | 83.3 ft-lb/in? | 80*10*3; ISO 180/1U |
93.0 kJ/m? @Temperature -30.0 °C | 44.3 ft-lb/in? @Temperature -22.0 °F | 80*10*3; ISO 180/1U | |
Charpy Impact Unnotched | NB | NB | Edgew 80*10*3 sp=62mm; ISO 179/1eU |
NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | Edgew 80*10*3 sp=62mm; ISO 179/1eU | |
Charpy Impact, Notched | 2.90 J/cm? | 13.8 ft-lb/in? | Edgew 80*10*3 sp=62mm; ISO 179/1eA |
1.00 J/cm? @Temperature -30.0 °C | 4.76 ft-lb/in? @Temperature -22.0 °F | Edgew 80*10*3 sp=62mm; ISO 179/1eA | |
Dart Drop, Total Energy | 43.0 J | 31.7 ft-lb | ASTM D3763 |
Thermal Properties | Metric | English | Comments |
CTE, linear, Parallel to Flow | 40.0 ?m/m-°C @Temperature -40.0 - 40.0 °C | 22.2 ?in/in-°F @Temperature -40.0 - 104 °F | ASTM E831 |
40.0 ?m/m-°C @Temperature 23.0 - 80.0 °C | 22.2 ?in/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 | |
CTE, linear, Transverse to Flow | 70.0 ?m/m-°C @Temperature -40.0 - 40.0 °C | 38.9 ?in/in-°F @Temperature -40.0 - 104 °F | ASTM E831 |
80.0 ?m/m-°C @Temperature 23.0 - 80.0 °C | 44.4 ?in/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 | |
Hot Ball Pressure Test | 125 °C | 257 °F | PASS; IEC 60695-10-2 |
Deflection Temperature at 0.46 MPa (66 psi) | 131 °C @Thickness 3.20 mm | 268 °F @Thickness 0.126 in | unannealed; ASTM D648 |
Deflection Temperature at 1.8 MPa (264 psi) | 125 °C @Thickness 3.20 mm | 257 °F @Thickness 0.126 in | unannealed; ASTM D648 |
Vicat Softening Point | 135 °C | 275 °F | Rate B/120; ISO 306 |
UL RTI, Electrical | 80.0 °C | 176 °F | UL 746B |
UL RTI, Mechanical with Impact | 80.0 °C | 176 °F | UL 746B |
UL RTI, Mechanical without Impact | 80.0 °C | 176 °F | UL 746B |
Flammability, UL94 | HB @Thickness >=0.400 mm | HB @Thickness >=0.0157 in | UL 94 |
Glow Wire Ignition Temperature | 900 °C @Thickness 2.00 mm | 1650 °F @Thickness 0.0787 in | IEC 60695-2-13 |
900 °C @Thickness 3.00 mm | 1650 °F @Thickness 0.118 in | IEC 60695-2-13 | |
930 °C @Thickness 1.00 mm | 1710 °F @Thickness 0.0394 in | IEC 60695-2-13 | |
Glow Wire Flammability Index | 930 °C @Thickness 1.00 mm | 1710 °F @Thickness 0.0394 in | IEC 60695-2-12 |
960 °C @Thickness 2.00 mm | 1760 °F @Thickness 0.0787 in | IEC 60695-2-12 | |
960 °C @Thickness 3.00 mm | 1760 °F @Thickness 0.118 in | IEC 60695-2-12 | |
Processing Properties | Metric | English | Comments |
Nozzle Temperature | 280 - 305 °C | 536 - 581 °F | |
Zone 2 | 275 - 300 °C | 527 - 572 °F | |
Zone 3 | 290 - 310 °C | 554 - 590 °F | |
Melt Temperature | 290 - 310 °C | 554 - 590 °F | Injection Molding |
Mold Temperature | 70.0 - 95.0 °C | 158 - 203 °F | |
Drying Temperature | 120 °C | 248 °F | Injection Molding |
Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Injection Molding |
48.0 hour | 48.0 hour | Cumulative; Injection Molding | |
Back Pressure | 0.300 - 0.700 MPa | 43.5 - 102 psi | |
Shot Size | 40 - 60 % | 40 - 60 % | |
Vent Depth | 0.00250 - 0.00760 cm | 0.000984 - 0.00299 in | |
Screw Speed | 40 - 70 rpm | 40 - 70 rpm |