| 是否进口：否 | 产地： 美国 | 厂家(产地)：沙伯基础(原GE) |
| 牌号：HFD4413 | 销售方式：品牌经销 | 类型：标准料 |
| 加工级别：注塑级 | 特性级别：标准级 | 用途级别：汽车部件、 电子电器部件、 运动器材、 家电部件、 电动工具配件 |
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.43 g/cc | 1.43 g/cc | ASTM D792 |
| Density | 1.44 g/cc | 0.0520 lb/in? | ISO 1183 |
| Moisture Absorption | 0.0200 % | 0.0200 % | Injection Molding |
| 0.120 % | 0.120 % | 23°C / 50% RH; ISO 62 | |
| Water Absorption at Saturation | 0.30 % | 0.30 % | ISO 62-1 |
| Viscosity | 18 cP @Load 1.20 kg, Temperature 300 °C | 18 cP @Load 2.65 lb, Temperature 572 °F | MVR cc/10 min; ISO 1133 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm | 0.0010 - 0.0030 in/in @Thickness 0.126 in | SABIC method |
| Linear Mold Shrinkage, Transverse | 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm | 0.0010 - 0.0030 in/in @Thickness 0.126 in | SABIC method |
| Melt Flow | 16 g/10 min @Load 1.20 kg, Temperature 300 °C | 16 g/10 min @Load 2.65 lb, Temperature 572 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 111 MPa | 16100 psi | 5 mm/min; ASTM D638 |
| 125 MPa | 18100 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 111 MPa | 16100 psi | 5 mm/min; ASTM D638 |
| 115 MPa | 16700 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 2.1 % | 2.1 % | 5 mm/min; ISO 527 |
| Elongation at Yield | 2.5 % | 2.5 % | 5 mm/min; ISO 527 |
| 3.0 % | 3.0 % | 5 mm/min; ASTM D638 | |
| Tensile Modulus | 7.87 GPa | 1140 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 182 MPa | 26400 psi | yld, 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 7.76 GPa | 1130 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact Notched | 133 J | 98.1 ft-lb | ASTM D256 |
| Izod Impact, Unnotched | 8.52 J/cm | 16.0 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m? | 4.76 ft-lb/in? | 80*10*3; ISO 180/1A |
| 10.0 kJ/m? @Temperature -30.0 °C | 4.76 ft-lb/in? @Temperature -22.0 °F | 80*10*3; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 37.0 kJ/m? | 17.6 ft-lb/in? | 80*10*3; ISO 180/1U |
| 30.0 kJ/m? @Temperature -30.0 °C | 14.3 ft-lb/in? @Temperature -22.0 °F | 80*10*3; ISO 180/1U | |
| Charpy Impact Unnotched | 4.00 J/cm? | 19.0 ft-lb/in? | Edgew 80*10*3 sp=62mm; ISO 179/1eU |
| 4.90 J/cm? @Temperature -30.0 °C | 23.3 ft-lb/in? @Temperature -22.0 °F | Edgew 80*10*3 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 1.20 J/cm? | 5.71 ft-lb/in? | Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| 1.10 J/cm? @Temperature -30.0 °C | 5.23 ft-lb/in? @Temperature -22.0 °F | Edgew 80*10*3 sp=62mm; ISO 179/1eA | |
| Dart Drop, Total Energy | 17.0 J | 12.5 ft-lb | ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 30.0 ?m/m-°C @Temperature -40.0 - 40.0 °C | 16.7 ?in/in-°F @Temperature -40.0 - 104 °F | ASTM E831 |
| 30.0 ?m/m-°C @Temperature 23.0 - 80.0 °C | 16.7 ?in/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 70.0 ?m/m-°C @Temperature -40.0 - 40.0 °C | 38.9 ?in/in-°F @Temperature -40.0 - 104 °F | ASTM E831 |
| 70.0 ?m/m-°C @Temperature 23.0 - 80.0 °C | 38.9 ?in/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 | |
| Hot Ball Pressure Test | 125 °C | 257 °F | PASS; IEC 60695-10-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C @Thickness 3.20 mm | 266 °F @Thickness 0.126 in | unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 129 °C | 264 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 125 °C @Thickness 3.20 mm | 257 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Vicat Softening Point | 143 °C | 289 °F | Rate B/120; ISO 306 |
| UL RTI, Electrical | 80.0 °C | 176 °F | UL 746B |
| UL RTI, Mechanical with Impact | 80.0 °C | 176 °F | UL 746B |
| UL RTI, Mechanical without Impact | 80.0 °C | 176 °F | UL 746B |
| Flammability, UL94 | HB @Thickness >=0.300 mm | HB @Thickness >=0.0118 in | UL 94 |
| Glow Wire Ignition Temperature | 850 °C @Thickness 1.00 mm | 1560 °F @Thickness 0.0394 in | IEC 60695-2-13 |
| 850 °C @Thickness 3.00 mm | 1560 °F @Thickness 0.118 in | IEC 60695-2-13 | |
| 875 °C @Thickness 2.00 mm | 1610 °F @Thickness 0.0787 in | IEC 60695-2-13 | |
| Glow Wire Flammability Index | 900 °C @Thickness 1.00 mm | 1650 °F @Thickness 0.0394 in | IEC 60695-2-12 |
| 960 °C @Thickness 2.00 mm | 1760 °F @Thickness 0.0787 in | IEC 60695-2-12 | |
| 960 °C @Thickness 3.00 mm | 1760 °F @Thickness 0.118 in | IEC 60695-2-12 | |
| Processing Properties | Metric | English | Comments |
| Nozzle Temperature | 280 - 305 °C | 536 - 581 °F | |
| Zone 2 | 275 - 300 °C | 527 - 572 °F | |
| Zone 3 | 290 - 310 °C | 554 - 590 °F | |
| Melt Temperature | 290 - 310 °C | 554 - 590 °F | Injection Molding |
| Mold Temperature | 70.0 - 95.0 °C | 158 - 203 °F | |
| Drying Temperature | 120 °C | 248 °F | Injection Molding |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Injection Molding |
| 48.0 hour | 48.0 hour | Cumulative; Injection Molding | |
| Back Pressure | 0.300 - 0.700 MPa | 43.5 - 102 psi | |
| Shot Size | 40 - 60 % | 40 - 60 % | |
| Vent Depth | 0.00250 - 0.00760 cm | 0.000984 - 0.00299 in | |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm |