| 是否进口：否 | 厂家(产地)：法国阿科码 | 牌号：2900-04 |
| 销售方式：品牌经销 | 类型：标准料 | 加工级别：注塑级、 挤出级 |
| 特性级别：标准级 | 用途级别：管材级、 电线电缆级、 电动工具配件、 薄壁制品 |
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.77 - 1.80 g/cc | 1.77 - 1.80 g/cc | ASTM D792 |
| Density | 1.78 g/cc | 0.0643 lb/in? | ISO 1183 |
| Water Absorption | 0.030 % | 0.030 % | Dry; Sim. to ISO 62 |
| 0.030 - 0.050 % | 0.030 - 0.050 % | ASTM D570 | |
| Viscosity | 600000 - 1.20e+6 cP @Shear Rate 100 1/s, Temperature 230 °C | 600000 - 1.20e+6 cP @Shear Rate 100 1/s, Temperature 446 °F | Melt; ASTM D3835 |
Melt Flow  | 9.0 g/10 min @Load 3.80 kg, Temperature 232 °C | 9.0 g/10 min @Load 8.38 lb, Temperature 450 °F | cm?/10 min Volumetric Rate; ISO 1133 |
| 4.0 - 21 g/10 min @Load 3.80 kg, Temperature 230 °C | 4.0 - 21 g/10 min @Load 8.38 lb, Temperature 446 °F | ASTM D1238 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 60 - 70 | 60 - 70 | ASTM D2240 |
| Tensile Strength at Break | 20.0 - 27.6 MPa | 2900 - 4000 psi | ASTM D638 |
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | Dry; ISO 527-1/-2 |
| 20.0 - 34.5 MPa | 2900 - 5000 psi | ASTM D638 | |
| Elongation at Break | >= 50 % | >= 50 % | Dry; ISO 527-1/-2 |
| 100 - 300 % | 100 - 300 % | ASTM D638 | |
| Elongation at Yield | 14.5 % | 14.5 % | Dry; ISO 527-1/-2 |
| 15 - 25 % | 15 - 25 % | ASTM D638 | |
| Tensile Modulus | 0.700 GPa | 102 ksi | Dry; ISO 527-1/-2 |
| 0.552 - 0.896 GPa | 80.1 - 130 ksi | ASTM D638 | |
| Flexural Strength | 20.7 - 34.5 MPa @Strain 5.00 % | 3000 - 5000 psi @Strain 5.00 % | ASTM D790 |
| Flexural Modulus | 0.483 - 0.758 GPa | 70.1 - 110 ksi | ASTM D790 |
| Compressive Strength | 31.0 - 41.4 MPa | 4500 - 6000 psi | ASTM D695 |
| Izod Impact, Notched | 5.34 - 10.7 J/cm | 10.0 - 20.0 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D256 |
| Coefficient of Friction, Dynamic | 0.33 | 0.33 | vs. steel; ASTM D1894 |
| Coefficient of Friction, Static | 0.33 | 0.33 | vs. steel; ASTM D1894 |
| Taber Abrasion, mg/1000 Cycles | 16 - 19 | 16 - 19 | CS 17 1000g:pad; ASTM-G195-13A |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 2.00e+14 ohm-cm | 2.00e+14 ohm-cm | 65% R.H; ASTM D257 |
| 2.00e+14 ohm-cm | 2.00e+14 ohm-cm | Dry; IEC 60093 | |
| Dielectric Constant | 3.5 - 10.6 @Frequency 1000 Hz | 3.5 - 10.6 @Frequency 1000 Hz | ASTM D150 |
| Dielectric Strength | 1.30 - 1.50 kV/mm | 33.0 - 38.1 kV/in | ASTM D149 |
| Dissipation Factor | 0.020 - 0.21 @Frequency 100000 Hz | 0.020 - 0.21 @Frequency 100000 Hz | ASTM D150 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 126 - 185 ?m/m-°C | 70.0 - 103 ?in/in-°F | ASTM D696 |
| Specific Heat Capacity | 0.745 - 0.958 J/g-°C | 0.178 - 0.229 BTU/lb-°F | DSC |
| Thermal Conductivity | 0.144 - 0.180 W/m-K | 0.999 - 1.25 BTU-in/hr-ft?-°F | ASTM D433 |
| Melting Point | 140 - 145 °C | 284 - 293 °F | ASTM D3418 |
| 143 °C | 289 °F | 10°C/min; Dry; ISO 11357-1/-3 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 60.0 - 75.0 °C | 140 - 167 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 40.0 - 55.0 °C | 104 - 131 °F | ASTM D648 |
| Glass Transition Temp, Tg | -41.1 - -39.4 °C | -42.0 - -38.9 °F | ASTM D7028 |
| -40.0 °C | -40.0 °F | 10°C/min; Dry; ISO 11357-1/-2 | |
| Decomposition Temperature | 375 °C | 707 °F | 1% wt. loss, TGA, in air |
| 410 °C | 770 °F | 1% wt. loss, TGA, in nitrogen | |
| Flammability, UL94 | V-0 @Thickness 0.800 mm | V-0 @Thickness 0.0315 in | IEC 60695-11-10 |
| V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | Yellow Card Available; Dry; IEC 60695-11-10 | |
| Oxygen Index | 75 % | 75 % | ASTM D2863 |
| 75 % | 75 % | Dry; ISO 4589-1/-2 | |
| Descriptive Properties | |||
| Moisture Sensitive | No |
本公司长期销售法国阿科玛 PVDF EBA EVA EEA EAA PA11 PA12 PMMAEMA料多种牌号
我司产品均可提供详细物性表(英文和中文版)相关资料；可开13%增值税发票；免费为客户分析样版并提供原料型号咨询服务(可免费帮客户翻译英文资料)；如需试料、了解产品相关信息及当日报价，敬请来电、竭诚为您服务！