| 是否进口：否 | 产地：美国 | 厂家(产地)：沙伯基础(原GE) |
| 牌号：VX3101N | 销售方式：品牌经销 | 类型：标准料 |
| 加工级别：注塑级 | 特性级别：标准级 | 用途级别：汽车部件、 电子电器部件、 运动器材、 家电部件、 电动工具配件 |
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in? | *** 1183 |
| Water Absorption | 0.34 % | 0.34 % | 23°C/sat; *** 62 |
| Moisture Absorption | 0.0800 % | 0.0800 % | 23°C / 50% RH; *** 62 |
| Linear Mold Shrinkage, Flow | 0.011 - 0.018 cm/cm | 0.011 - 0.018 in/in | SABIC method |
| Linear Mold Shrinkage, Transverse | 0.0090 - 0.018 cm/cm | 0.0090 - 0.018 in/in | SABIC method |
| Melt Flow | 20 g/10 min @Load 1.20 kg, Temperature 250 °C | 20 g/10 min @Load 2.65 lb, Temperature 482 °F | cm?/10 min; *** 1133 |
| Mechanical Properties | Metric | English | Comments |
| Ball Indentation Hardness | 100 MPa | 14500 psi | *** 2039-1 |
| Tensile Strength at Break | 50.0 MPa | 7250 psi | 50 mm/min; *** 527 |
| Tensile Strength, Yield | 65.0 MPa | 9430 psi | 50 mm/min; *** 527 |
| Elongation at Break | 15 % | 15 % | 50 mm/min; *** 527 |
| Elongation at Yield | 3.5 % | 3.5 % | 50 mm/min; *** 527 |
| Tensile Modulus | 2.80 GPa | 406 ksi | 1mm/min; *** 527 |
| Flexural Yield Strength | 85.0 MPa | 12300 psi | 2 mm/min; *** 178 |
| Flexural Modulus | 2.60 GPa | 377 ksi | 2 mm/min; *** 178 |
| Izod Impact, Notched (***) | 4.00 kJ/m? | 1.90 ft-lb/in? | 80*10*4; *** 180/1A |
| 2.00 kJ/m? @Temperature -30.0 °C | 0.952 ft-lb/in? @Temperature -22.0 °F | 80*10*4; *** 180/1A | |
| 2.00 kJ/m? @Temperature 0.000 °C | 0.952 ft-lb/in? @Temperature 32.0 °F | 80*10*4; *** 180/1A | |
| Izod Impact, Unnotched (***) | NB | NB | 80*10*4; *** 180/1U |
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | 80*10*4; *** 180/1U | |
| Charpy Impact Unnotched | NB | NB | Edgew 80*10*4 sp=62mm; *** 179/1eU |
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | Edgew 80*10*4 sp=62mm; *** 179/1eU | |
| Charpy Impact, Notched | 0.500 J/cm? | 2.38 ft-lb/in? | Edgew 80*10*4 sp=62mm; *** 179/1eA |
| 0.300 J/cm? @Temperature -30.0 °C | 1.43 ft-lb/in? @Temperature -22.0 °F | Edgew 80*10*4 sp=62mm; *** 179/1eA | |
| Taber Abrasion, mg/1000 Cycles | 9.0 | 9.0 | CS-17, 1 kg; SABIC method |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 |
| Dielectric Constant | 2.9 @Frequency 1.00e+6 Hz | 2.9 @Frequency 1.00e+6 Hz | IEC 60250 |
| 3.1 @Frequency 50.0 - 60.0 Hz | 3.1 @Frequency 50.0 - 60.0 Hz | IEC 60250 | |
| Dielectric Strength | 16.0 kV/mm @Thickness 3.20 mm | 406 kV/in @Thickness 0.126 in | in oil; IEC 60243-1 |
| Dissipation Factor | 0.0020 @Frequency 50.0 - 60.0 Hz | 0.0020 @Frequency 50.0 - 60.0 Hz | IEC 60250 |
| 0.020 @Frequency 1.00e+6 Hz | 0.020 @Frequency 1.00e+6 Hz | IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 130 ?m/m-°C @Temperature 23.0 - 60.0 °C | 72.2 ?in/in-°F @Temperature 73.4 - 140 °F | *** 11359-2 |
| CTE, linear, Transverse to Flow | 130 ?m/m-°C @Temperature 23.0 - 60.0 °C | 72.2 ?in/in-°F @Temperature 73.4 - 140 °F | *** 11359-2 |
| Hot Ball Pressure Test | 125 °C | 257 °F | IEC 60695-10-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | Edgew 120*10*4 sp=100mm; *** 75/Be |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | 1.8 MPa Edgew 120*10*4 sp=100mm; *** 75/Ae |
| Vicat Softening Point | 183 °C | 361 °F | Rate B/50; *** 306 |
| 185 °C | 365 °F | Rate B/120; *** 306 | |
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | UL 94 by SABIC-IP |
| Oxygen Index | 20 % | 20 % | *** 4589 |
| Glow Wire Test | 850 °C @Thickness 1.00 mm | 1560 °F @Thickness 0.0394 in | IEC 60695-2-12 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 40.0 - 60.0 °C | 104 - 140 °F | Hopper Temperature |
| Nozzle Temperature | 240 - 260 °C | 464 - 500 °F | Injection Molding |
| Zone 1 | 230 - 245 °C | 446 - 473 °F | |
| Zone 2 | 240 - 255 °C | 464 - 491 °F | |
| Zone 3 | 245 - 265 °C | 473 - 509 °F | |
| Melt Temperature | 250 - 270 °C | 482 - 518 °F | |
| Mold Temperature | 40.0 - 100 °C | 104 - 212 °F | |
| Drying Temperature | 110 - 120 °C | 230 - 248 °F | Injection Molding |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | Injection Molding |
| Moisture Content | 0.020 % | 0.020 % |