是否进口:否 | 产地:美国 | 厂家(产地):沙伯基础(原GE) |
牌号:LUX9130C | 销售方式:品牌经销 | 类型:标准料 |
加工级别:注塑级 | 特性级别:标准级 | 用途级别:汽车部件、 电子电器部件、 运动器材、 家电部件、 电动工具配件 |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
Density | 1.20 g/cc | 0.0434 lb/in? | ISO 1183 |
Moisture Absorption | 0.0200 % | 0.0200 % | Injection Molding |
0.110 % | 0.110 % | 23°C / 50% RH; ISO 62 | |
Water Absorption at Saturation | 0.13 % | 0.13 % | ISO 62-1 |
Viscosity | 17 cP @Load 1.20 kg, Temperature 300 °C | 17 cP @Load 2.65 lb, Temperature 572 °F | MVR cc/10 min; ISO 1133 |
Linear Mold Shrinkage, Flow | 0.0055 - 0.0075 cm/cm @Thickness 3.20 mm | 0.0055 - 0.0075 in/in @Thickness 0.126 in | SABIC method |
Linear Mold Shrinkage, Transverse | 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm | 0.0060 - 0.0080 in/in @Thickness 0.126 in | SABIC method |
Melt Flow | 18 g/10 min @Load 1.20 kg, Temperature 300 °C | 18 g/10 min @Load 2.65 lb, Temperature 572 °F | ASTM D1238 |
Mechanical Properties | Metric | English | Comments |
Ball Indentation Hardness | 138 MPa | 20000 psi | H358/30; ISO 2039-1 |
Tensile Strength at Break | 54.0 MPa | 7830 psi | 50 mm/min; ASTM D638 |
57.0 MPa | 8270 psi | 50 mm/min; ISO 527 | |
Tensile Strength, Yield | 63.0 MPa | 9140 psi | 50 mm/min; ISO 527 |
67.0 MPa | 9720 psi | 50 mm/min; ASTM D638 | |
Elongation at Break | 73 % | 73 % | 50 mm/min; ISO 527 |
80 % | 80 % | 50 mm/min; ASTM D638 | |
Elongation at Yield | 6.0 % | 6.0 % | 50 mm/min; ASTM D638 |
6.0 % | 6.0 % | 50 mm/min; ISO 527 | |
Tensile Modulus | 2.30 GPa | 334 ksi | 1 mm/min; ISO 527 |
2.40 GPa | 348 ksi | 50 mm/min; ASTM D638 | |
Flexural Strength | 96.0 MPa | 13900 psi | yield, 2 mm/min; ISO 178 |
103 MPa | 14900 psi | yld, 1.3 mm/min, 50 mm span; ASTM D790 | |
Flexural Modulus | 2.40 GPa | 348 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
2.40 GPa | 348 ksi | 2 mm/min; ISO 178 | |
Izod Impact Notched | 100 J | 73.8 ft-lb | ASTM D256 |
85.0 J @Temperature -30.0 °C | 62.7 ft-lb @Temperature -22.0 °F | ASTM D256 | |
Izod Impact, Unnotched | NB | NB | ASTM D4812 |
NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ASTM D4812 | |
Izod Impact, Notched (ISO) | 10.0 kJ/m? | 4.76 ft-lb/in? | 80*10*3; ISO 180/1A |
9.00 kJ/m? @Temperature -30.0 °C | 4.28 ft-lb/in? @Temperature -22.0 °F | 80*10*3; ISO 180/1A | |
Izod Impact, Unnotched (ISO) | NB | NB | 80*10*3; ISO 180/1U |
NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | 80*10*3; ISO 180/1U | |
Charpy Impact Unnotched | NB | NB | Edgew 80*10*3 sp=62mm; ISO 179/1eU |
NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | Edgew 80*10*3 sp=62mm; ISO 179/1eU | |
Charpy Impact, Notched | 1.00 J/cm? | 4.76 ft-lb/in? | Edgew 80*10*3 sp=62mm; ISO 179/1eA |
0.900 J/cm? @Temperature -30.0 °C | 4.28 ft-lb/in? @Temperature -22.0 °F | Edgew 80*10*3 sp=62mm; ISO 179/1eA | |
Dart Drop, Total Energy | 65.0 J | 47.9 ft-lb | ASTM D3763 |
Electrical Properties | Metric | English | Comments |
Volume Resistivity | 1.00e+16 - 1.00e+17 ohm-cm | 1.00e+16 - 1.00e+17 ohm-cm | IEC 62631-3-1 |
Surface Resistance | 1.00e+16 - 1.00e+17 ohm | 1.00e+16 - 1.00e+17 ohm | ROA; IEC 62631-3-2 |
Dielectric Constant | 2.4 @Frequency 50.0 - 60.0 Hz | 2.4 @Frequency 50.0 - 60.0 Hz | IEC 62631-2-1 |
2.7 @Frequency 1.00e+6 Hz | 2.7 @Frequency 1.00e+6 Hz | IEC 62631-2-1 | |
2.78 @Frequency 1.10e+9 Hz | 2.78 @Frequency 1.10e+9 Hz | ASTM ES 7-83 | |
Dielectric Strength | 18.0 kV/mm @Thickness 3.20 mm | 457 kV/in @Thickness 0.126 in | in oil; IEC 60243-1 |
26.0 kV/mm @Thickness 1.60 mm | 660 kV/in @Thickness 0.0630 in | in oil; IEC 60243-1 | |
34.0 kV/mm @Thickness 0.800 mm | 864 kV/in @Thickness 0.0315 in | in oil; IEC 60243-1 | |
Dissipation Factor | 0.0010 @Frequency 50.0 - 60.0 Hz | 0.0010 @Frequency 50.0 - 60.0 Hz | IEC 62631-2-1 |
0.0056 @Frequency 1.10e+9 Hz | 0.0056 @Frequency 1.10e+9 Hz | ASTM ES 7-83 | |
0.010 @Frequency 1.00e+6 Hz | 0.010 @Frequency 1.00e+6 Hz | IEC 62631-2-1 | |
Comparative Tracking Index | 175 - 250 V | 175 - 250 V | UL 746A |
Hot Wire Ignition, HWI | 15 - 30 sec @Thickness >=0.400 mm | 15 - 30 sec @Thickness >=0.0157 in | UL 746A |
>= 120 sec @Thickness >=1.50 mm | >= 120 sec @Thickness >=0.0591 in | UL 746A | |
High Amp Arc Ignition, HAI | 60 - 120 arcs @Thickness >=0.400 mm | 60 - 120 arcs @Thickness >=0.0157 in | UL 746A |
Thermal Properties | Metric | English | Comments |
CTE, linear, Parallel to Flow | 68.0 ?m/m-°C @Temperature -40.0 - 40.0 °C | 37.8 ?in/in-°F @Temperature -40.0 - 104 °F | ASTM E831 |
77.0 ?m/m-°C @Temperature 23.0 - 80.0 °C | 42.8 ?in/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 | |
CTE, linear, Transverse to Flow | 70.0 ?m/m-°C @Temperature -40.0 - 40.0 °C | 38.9 ?in/in-°F @Temperature -40.0 - 104 °F | ASTM E831 |
80.0 ?m/m-°C @Temperature 23.0 - 80.0 °C | 44.4 ?in/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 | |
Hot Ball Pressure Test | 125 °C | 257 °F | PASS; IEC 60695-10-2 |
Deflection Temperature at 0.46 MPa (66 psi) | 131 °C | 268 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
130 °C @Thickness 3.20 mm | 266 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
Deflection Temperature at 1.8 MPa (264 psi) | 121 °C | 250 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
120 °C @Thickness 3.20 mm | 248 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
Vicat Softening Point | 136 °C | 277 °F | Rate B/50; ASTM D1525 |
139 °C | 282 °F | Rate B/50; ISO 306 | |
140 °C | 284 °F | Rate B/120; ISO 306 | |
146 °C | 295 °F | Rate A/50; ISO 306 | |
UL RTI, Electrical | 130 °C | 266 °F | UL 746B |
UL RTI, Mechanical with Impact | 120 °C | 248 °F | UL 746B |
UL RTI, Mechanical without Impact | 130 °C | 266 °F | UL 746B |
Flammability, UL94 | V-2 @Thickness >=0.400 mm | V-2 @Thickness >=0.0157 in | UL 94 |
V-0 @Thickness >=1.50 mm | V-0 @Thickness >=0.0591 in | UL 94 | |
Glow Wire Ignition Temperature | 850 °C @Thickness 1.50 mm | 1560 °F @Thickness 0.0591 in | IEC 60695-2-13 |
850 °C @Thickness 3.00 mm | 1560 °F @Thickness 0.118 in | IEC 60695-2-13 | |
Glow Wire Flammability Index | 960 °C @Thickness 1.50 mm | 1760 °F @Thickness 0.0591 in | IEC 60695-2-12 |
960 °C @Thickness 3.00 mm | 1760 °F @Thickness 0.118 in | IEC 60695-2-12 | |
Optical Properties | Metric | English | Comments |
Transmission, Visible | >= 91 % @Thickness 2.54 mm | >= 91 % @Thickness 0.100 in | ASTM D1003 |
Processing Properties | Metric | English | Comments |
Nozzle Temperature | 275 - 300 °C | 527 - 572 °F | |
Zone 2 | 270 - 295 °C | 518 - 563 °F | |
Zone 3 | 280 - 305 °C | 536 - 581 °F | |
Melt Temperature | 280 - 305 °C | 536 - 581 °F | Injection Molding |
Mold Temperature | 70.0 - 95.0 °C | 158 - 203 °F | |
Drying Temperature | 120 °C | 248 °F | Injection Molding |
Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Injection Molding |
48.0 hour | 48.0 hour | Cumulative; Injection Molding | |
Back Pressure | 0.300 - 0.700 MPa | 43.5 - 102 psi | |
Shot Size | 40 - 60 % | 40 - 60 % | |
Vent Depth | 0.00250 - 0.00760 cm | 0.000984 - 0.00299 in | |
Screw Speed | 40 - 70 rpm | 40 - 70 rpm | |
Descriptive Properties | |||
UV-light, water exposure/immersion | F1 | UL 746C |
本公司长期销售沙伯基础 PC,ABS,ASA,EVA,PA6,PBT,PE,PBT,PET,PMMA,POM,PS,PP,PU,PES,PEI料等多种牌号
我司产品均可提供详细物性表(英文和中文版)相关资料;可开13%增值税发票;免费为客户分析样版并提供原料型号咨询服务(可免费帮客户翻译英文资料);如需试料、了解产品相关信息及当日报价,敬请来电、竭诚为您服务!