是否进口:否 | 产地:美国 | 厂家(产地):沙伯基础(原GE) |
牌号:HPH4404 | 销售方式:品牌经销 | 类型:标准料 |
加工级别:注塑级 | 特性级别:标准级 | 用途级别:汽车部件、 电子电器部件、 运动器材、 家电部件、 电动工具配件 |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
1.205 g/cc | 1.205 g/cc | ASTM D792 | |
Density | 1.19 g/cc | 0.0430 lb/in? | ASTM D792 |
1.20 g/cc | 0.0434 lb/in? | ISO 1183 | |
Water Absorption | 0.16 % @Time 86400 sec | 0.16 % @Time 24.0 hour | ASTM D570 |
Moisture Absorption | 0.0200 % | 0.0200 % | Injection Molding |
0.350 % | 0.350 % | 23°C / 50% RH; ISO 62 | |
Water Absorption at Saturation | 0.16 % | 0.16 % | ISO 62-1 |
Viscosity | 29 cP @Load 2.16 kg, Temperature 330 °C | 29 cP @Load 4.76 lb, Temperature 626 °F | MVR cc/10 min; ISO 1133 |
Linear Mold Shrinkage, Flow | 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm | 0.0060 - 0.0080 in/in @Thickness 0.126 in | SABIC method |
Melt Flow | 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C | 6.0 g/10 min @Load 2.65 lb, Temperature 572 °F | ASTM D1238 |
30 g/10 min @Load 2.16 kg, Temperature 330 °C | 30 g/10 min @Load 4.76 lb, Temperature 626 °F | ASTM D1238 | |
Mechanical Properties | Metric | English | Comments |
Hardness, Rockwell M | 85 | 85 | ASTM D785 |
Hardness, Rockwell R | 122 | 122 | ASTM D785 |
Tensile Strength at Break | 60.0 MPa | 8700 psi | 50 mm/min; ISO 527 |
70.0 MPa | 10200 psi | 50 mm/min; ASTM D638 | |
Tensile Strength, Yield | 65.0 MPa | 9430 psi | 50 mm/min; ASTM D638 |
65.0 MPa | 9430 psi | 50 mm/min; ISO 527 | |
Elongation at Break | 85 % | 85 % | 50 mm/min; ISO 527 |
>= 112 % | >= 112 % | 50 mm/min; ASTM D638 | |
Elongation at Yield | 7.0 % | 7.0 % | 50 mm/min; ASTM D638 |
7.0 % | 7.0 % | 50 mm/min; ISO 527 | |
Tensile Modulus | 2.10 GPa | 305 ksi | 5 mm/min; ASTM D638 |
2.15 GPa | 312 ksi | 1 mm/min; ISO 527 | |
Flexural Strength | 66.0 MPa | 9570 psi | yield, 2 mm/min; ISO 178 |
95.0 MPa | 13800 psi | yld, 1.3 mm/min, 50 mm span; ASTM D790 | |
Flexural Modulus | 2.12 GPa | 307 ksi | 2 mm/min; ISO 178 |
2.20 GPa | 319 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
Izod Impact Notched | 600 J | 443 ft-lb | ASTM D256 |
120 J @Temperature -30.0 °C | 88.5 ft-lb @Temperature -22.0 °F | ASTM D256 | |
Izod Impact, Unnotched | NB | NB | ASTM D4812 |
Izod Impact, Notched (ISO) | 53.0 kJ/m? | 25.2 ft-lb/in? | 80*10*3; ISO 180/1A |
11.0 kJ/m? @Temperature -30.0 °C | 5.23 ft-lb/in? @Temperature -22.0 °F | 80*10*3; ISO 180/1A | |
Izod Impact, Unnotched (ISO) | NB | NB | 80*10*3; ISO 180/1U |
NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | 80*10*3; ISO 180/1U | |
Charpy Impact Unnotched | NB | NB | Edgew 80*10*3 sp=62mm; ISO 179/1eU |
NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | Edgew 80*10*3 sp=62mm; ISO 179/1eU | |
Charpy Impact, Notched | 5.70 J/cm? | 27.1 ft-lb/in? | Edgew 80*10*3 sp=62mm; ISO 179/1eA |
1.30 J/cm? @Temperature -30.0 °C | 6.19 ft-lb/in? @Temperature -22.0 °F | Edgew 80*10*3 sp=62mm; ISO 179/1eA | |
Tensile Impact Strength | 577 kJ/m? | 275 ft-lb/in? | ASTM D1822 |
Dart Drop, Total Energy | 120 J | 88.5 ft-lb | ASTM D3763 |
149 J | 110 ft-lb | ASTM D3029 | |
Electrical Properties | Metric | English | Comments |
Volume Resistivity | >= 2.60e+17 ohm-cm | >= 2.60e+17 ohm-cm | ASTM D257 |
Dielectric Constant | 3.0 @Frequency 1.00e+6 Hz | 3.0 @Frequency 1.00e+6 Hz | ASTM D150 |
3.15 @Frequency 50.0 - 60.0 Hz | 3.15 @Frequency 50.0 - 60.0 Hz | ASTM D150 | |
Dielectric Strength | 20.2 kV/mm @Thickness 3.20 mm | 513 kV/in @Thickness 0.126 in | in air; ASTM D149 |
Dissipation Factor | 0.0012 @Frequency 50.0 - 60.0 Hz | 0.0012 @Frequency 50.0 - 60.0 Hz | ASTM D150 |
0.024 @Frequency 100 Hz | 0.024 @Frequency 100 Hz | ASTM D150 | |
Thermal Properties | Metric | English | Comments |
CTE, linear, Parallel to Flow | 60.0 ?m/m-°C @Temperature -40.0 - 40.0 °C | 33.3 ?in/in-°F @Temperature -40.0 - 104 °F | ASTM E831 |
60.0 ?m/m-°C @Temperature -40.0 - 40.0 °C | 33.3 ?in/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
CTE, linear, Transverse to Flow | 60.0 ?m/m-°C @Temperature -40.0 - 40.0 °C | 33.3 ?in/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 |
80.0 ?m/m-°C @Temperature -40.0 - 40.0 °C | 44.4 ?in/in-°F @Temperature -40.0 - 104 °F | ASTM E831 | |
Specific Heat Capacity | 1.25 J/g-°C | 0.299 BTU/lb-°F | ASTM C351 |
Thermal Conductivity | 0.210 W/m-K | 1.46 BTU-in/hr-ft?-°F | ASTM C177 |
Deflection Temperature at 1.8 MPa (264 psi) | 125 °C | 257 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
142 °C @Thickness 3.20 mm | 288 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
Vicat Softening Point | 154 °C | 309 °F | Rate B/50; ISO 306 |
155 °C | 311 °F | Rate B/120; ISO 306 | |
160 °C | 320 °F | Rate B/50; ASTM D1525 | |
UL RTI, Electrical | 80.0 °C | 176 °F | UL 746B |
UL RTI, Mechanical with Impact | 80.0 °C | 176 °F | UL 746B |
UL RTI, Mechanical without Impact | 80.0 °C | 176 °F | UL 746B |
Flammability, UL94 | HB @Thickness >=0.750 mm | HB @Thickness >=0.0295 in | UL 94 |
Optical Properties | Metric | English | Comments |
Refractive Index | 1.60 | 1.60 | ASTM D542 |
Haze | 1.0 % @Thickness 2.54 mm | 1.0 % @Thickness 0.100 in | ASTM D1003 |
Transmission, Visible | 85 % @Thickness 2.54 mm | 85 % @Thickness 0.100 in | ASTM D1003 |
Processing Properties | Metric | English | Comments |
Nozzle Temperature | 290 - 310 °C | 554 - 590 °F | |
Zone 2 | 280 - 305 °C | 536 - 581 °F | |
Zone 3 | 295 - 315 °C | 563 - 599 °F | |
Melt Temperature | 295 - 315 °C | 563 - 599 °F | Injection Molding |
Mold Temperature | 70.0 - 95.0 °C | 158 - 203 °F | |
Drying Temperature | 120 °C | 248 °F | Injection Molding |
Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Injection Molding |
48.0 hour | 48.0 hour | Cumulative; Injection Molding | |
Back Pressure | 0.300 - 0.700 MPa | 43.5 - 102 psi | |
Shot Size | 40 - 60 % | 40 - 60 % | |
Vent Depth | 0.00250 - 0.00760 cm | 0.000984 - 0.00299 in | |
Screw Speed | 40 - 70 rpm | 40 - 70 rpm |
本公司长期销售沙伯基础 PC,ABS,ASA,EVA,PA6,PBT,PE,PBT,PET,PMMA,POM,PS,PP,PU,PES,PEI料等多种牌号
我司产品均可提供详细物性表(英文和中文版)相关资料;可开13%增值税发票;免费为客户分析样版并提供原料型号咨询服务(可免费帮客户翻译英文资料);如需试料、了解产品相关信息及当日报价,敬请来电、竭诚为您服务!