| 是否进口：否 | 产地：美国 | 厂家(产地)：沙伯基础(原GE) |
| 牌号：CXT17EX | 销售方式：品牌经销 | 类型：标准料 |
| 加工级别：注塑级 | 特性级别：标准级 | 用途级别：汽车部件、 电子电器部件、 运动器材、 家电部件、 电动工具配件 |
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.21 g/cc | 1.21 g/cc | ASTM D792 |
| Density | 1.21 g/cc | 0.0437 lb/in? | ISO 1183 |
| Moisture Absorption | 0.300 % | 0.300 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.30 % | 0.30 % | ISO 62-1 |
| Viscosity | 27 cP @Load 2.16 kg, Temperature 330 °C | 27 cP @Load 4.76 lb, Temperature 626 °F | MVR cc/10 min; ISO 1133 |
| Linear Mold Shrinkage, Flow | 0.0070 - 0.0095 cm/cm @Thickness 3.20 mm | 0.0070 - 0.0095 in/in @Thickness 0.126 in | SABIC method |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0095 cm/cm @Thickness 3.20 mm | 0.0070 - 0.0095 in/in @Thickness 0.126 in | SABIC method |
| Melt Flow | 30 g/10 min @Load 2.16 kg, Temperature 330 °C | 30 g/10 min @Load 4.76 lb, Temperature 626 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 60.0 MPa | 8700 psi | 50 mm/min; ASTM D638 |
| 60.0 MPa | 8700 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 75.0 MPa | 10900 psi | 50 mm/min; ASTM D638 |
| 75.0 MPa | 10900 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | >= 40 % | >= 40 % | 50 mm/min; ASTM D638 |
| >= 50 % | >= 50 % | 50 mm/min; ISO 527 | |
| Elongation at Yield | 6.5 % | 6.5 % | 50 mm/min; ISO 527 |
| 7.0 % | 7.0 % | 50 mm/min; ASTM D638 | |
| Tensile Modulus | 2.45 GPa | 355 ksi | 1 mm/min; ISO 527 |
| 2.50 GPa | 363 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 110 MPa | 16000 psi | yield, 2 mm/min; ISO 178 |
| 120 MPa | 17400 psi | yld, 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 2.45 GPa | 355 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 2.50 GPa | 363 ksi | 2 mm/min; ISO 178 | |
| Izod Impact Notched | 80.0 J | 59.0 ft-lb | ASTM D256 |
| 75.0 J @Temperature -30.0 °C | 55.3 ft-lb @Temperature -22.0 °F | ASTM D256 | |
| Izod Impact, Notched (ISO) | 8.00 kJ/m? | 3.81 ft-lb/in? | 80*10*3; ISO 180/1A |
| 7.00 kJ/m? @Temperature -30.0 °C | 3.33 ft-lb/in? @Temperature -22.0 °F | 80*10*3; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB | NB | 80*10*3; ISO 180/1U |
| Charpy Impact Unnotched | NB | NB | Edgew 80*10*3 sp=62mm; ISO 179/1eU |
| Charpy Impact, Notched | 1.00 J/cm? | 4.76 ft-lb/in? | Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| 0.700 J/cm? @Temperature -30.0 °C | 3.33 ft-lb/in? @Temperature -22.0 °F | Edgew 80*10*3 sp=62mm; ISO 179/1eA | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 60.0 ?m/m-°C @Temperature -40.0 - 40.0 °C | 33.3 ?in/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 60.0 ?m/m-°C @Temperature -40.0 - 40.0 °C | 33.3 ?in/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 |
| Thermal Conductivity | 0.200 W/m-K | 1.39 BTU-in/hr-ft?-°F | ISO 8302 |
| Deflection Temperature at 0.46 MPa (66 psi) | 167 °C | 333 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 167 °C @Thickness 3.20 mm | 333 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 154 °C | 309 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 154 °C @Thickness 3.20 mm | 309 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Vicat Softening Point | 174 °C | 345 °F | Rate B/120; ASTM D1525 |
| 174 °C | 345 °F | Rate B/120; ISO 306 | |
| Glass Transition Temp, Tg | 175 °C | 347 °F | half width; SABIC method |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.602 | 1.602 | ISO 489 |
| Abbe Number | 30 | 30 | ISO 489 |
| Transmission, Visible | 87 % @Thickness 3.00 mm | 87 % @Thickness 0.118 in | ASTM D1003 |
| 88 % @Thickness 2.00 mm | 88 % @Thickness 0.0787 in | ASTM D1003 | |
| 89 % @Thickness 1.00 mm | 89 % @Thickness 0.0394 in | ASTM D1003 | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 90.0 - 150 °C | 194 - 302 °F | Calibrator Temperature |
| Zone 1 | 160 - 230 °C | 320 - 446 °F | Multiwall Sheet Extrusion |
| Zone 2 | 250 - 290 °C | 482 - 554 °F | Multiwall Sheet Extrusion |
| Zone 3 | 280 - 345 °C | 536 - 653 °F | Multiwall Sheet Extrusion |
| Adapter Temperature | 80.0 - 130 °C | 176 - 266 °F | Multiwall Sheet Extrusion |
| Die Temperature | 270 - 350 °C | 518 - 662 °F | Multiwall Sheet Extrusion |
| Melt Temperature | 270 - 350 °C | 518 - 662 °F | Multiwall Sheet Extrusion |
| Drying Temperature | 135 °C | 275 °F | Multiwall Sheet Extrusion |
| Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour | Multiwall Sheet Extrusion |
| Precipitation Temperature | 40.0 - 60.0 °C | 104 - 140 °F | Hopper Temperature |