| 是否进口：否 | 产地：美国 | 厂家(产地)：美国塞拉尼斯 |
| 牌号：S 9063 | 销售方式：品牌经销 | 类型：标准料 |
| 加工级别：注塑级 | 特性级别：增韧级、 标准级 | 用途级别：汽车部件、 电子电器部件、 运动器材、 电动工具配件 |
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in? | 10x10x4 mm from multi-purpose test specimen (ISO 3167); ISO 1183 |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 80x80x1mm, at 23°C and 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.65 % | 0.65 % | 80x80x1mm, 23°C; ISO 62 |
| Melt Flow | 11.12 g/10 min @Load 2.16 kg, Temperature 190 °C | 11.12 g/10 min @Load 4.76 lb, Temperature 374 °F | Calculated from Volume flow Rate: 8 cm3/10min; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Ball Indentation Hardness | 110 MPa | 16000 psi | 30 sec value, 20x20x4 mm; ISO 2039, part 1; applied load 358 N |
| Tensile Strength, Yield | 53.0 MPa | 7690 psi | multi-purpose test specimen (ISO 3167); ISO 527, part 1/2; test speed 50 mm/min |
| Elongation at Break | 32 % | 32 % | multi-purpose specimen (ISO 3167); ISO 527, part 1/2; test speed 50 mm/min |
| Elongation at Yield | 9.0 % | 9.0 % | multi-purpose test specimen (ISO 3167); ISO 527, part 1/2; test speed 50 mm/min |
| Tensile Modulus | 2.10 GPa | 305 ksi | multi-purpose test specimen (ISO 3167); ISO 527, part 1/2; test speed 1 mm/min |
| Flexural Modulus | 2.00 GPa | 290 ksi | 80x10x4mm from multi-purpose test specimen (ISO 3167); ISO 178 |
| Charpy Impact Unnotched | 22.0 J/cm? @Temperature -30.0 °C | 105 ft-lb/in? @Temperature -22.0 °F | 80x10x4 m from multi-purpose test specimen (ISO 3167); ISO 179 1eU |
| 25.0 J/cm? @Thickness 4.00 mm, Temperature 23.0 °C | 119 ft-lb/in? @Thickness 0.157 in, Temperature 73.4 °F | 80x10x4 m from multi-purpose test specimen (ISO 3167); ISO 179 1eU | |
| Charpy Impact, Notched | 0.700 J/cm? @Temperature -30.0 °C | 3.33 ft-lb/in? @Temperature -22.0 °F | 80x10x4 m from multi-purpose test specimen (ISO 3167); ISO 179 1eA |
| 1.20 J/cm? @Thickness 4.00 mm, Temperature 23.0 °C | 5.71 ft-lb/in? @Thickness 0.157 in, Temperature 73.4 °F | 80x10x4 m from multi-purpose test specimen (ISO 3167); ISO 179 1eA | |
| Penetration | 8.0 | 8.0 | mm, deformation damage, 60x60x3mm; ISO 6603, part 2 |
| 20 | 20 | J, work to damage, 60x60x3 mm; ISO 6603, part 2 | |
| Tensile Creep Modulus, 1 hour | 1800 MPa | 261000 psi | multi-purpose test specimen (ISO 3167); ISO 899, part 1 |
| Tensile Creep Modulus, 1000 hours | 1000 MPa | 145000 psi | multi-purpose test specimen (ISO 3167); ISO 899, part 1 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 4.2 @Frequency 100 Hz | 4.2 @Frequency 100 Hz | 80x80x1 mm; IEC 60250 |
| 4.2 @Frequency 1e+6 Hz | 4.2 @Frequency 1e+6 Hz | 80x80x1 mm; IEC 60250 | |
| Dielectric Strength | 28.0 kV/mm | 711 kV/in | 80x80x1 mm; IEC 60243, part 1 |
| Dissipation Factor | 0.0050 @Frequency 100 Hz | 0.0050 @Frequency 100 Hz | 80x80x1 mm; IEC 60250 |
| 0.015 @Frequency 1e+6 Hz | 0.015 @Frequency 1e+6 Hz | 80x80x1 mm; IEC 60250 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 120 ?m/m-°C @Temperature 23.0 - 55.0 °C | 66.7 ?in/in-°F @Temperature 73.4 - 131 °F | Longitudinal, 30x10x4 mm from multi-purpose test specimen (ISO 3167); ISO 11359, part 1/2 |
| Melting Point | 166 °C | 331 °F | DSC, 10 K/min, Molding compound; ISO 3146, method C1b |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.0 °C | 180 °F | 80x10x4 mm from multi-purpose test specimen (ISO 3167); ISO 75, part 1/2 |
| Vicat Softening Point | 140 °C | 284 °F | VST/B/50, 10x10x4 mm from multi-purpose test specimen (ISO 3167); ISO 306 |
本公司长期销售 美国塞拉尼斯 POM料多种型号
我司产品均可提供详细物性表(英文和中文版)相关资料；可开13%增值税发票；免费为客户分析样版并提供原料型号咨询服务(可免费帮客户翻译英文资料)；如需试料、了解产品相关信息及当日报价，敬请来电，竭诚为您服务！